Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 44 %
Density: 1.046 g/ml
Brand: SWANCOR
Appearance: Clear amber liquid
Solid Content: 58±1.5%
Viscosity: 380±100 cps
Gel Time: 15-25 min
HDT: 106-110°C
Barcol Hardness: 40±3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：35000-60000 mPa.s);（Typical Value Base Gelcoat Spray：21000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand: Aliancys (Neogel)
Type: Air-drying repair gelcoat
Gel time at 25℃: TM 2245: 8-15 minutes
Coating thickness: not less than 0.3-0.5 mm
MEKP hardener dosage: 1%-2% (50% solution)
Brand：AOC
Appearance：Hazy
Viscosity, 23°C：200 – 700 mPa.s
Gel time from 25 to 35°C：14 – 45 minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):（Typical Value Base Gelcoat Spray：42500-52000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand:SANMU
Appearance：Transparent liquid, free of visible mechanical impurities
Epoxy equivalent (g / eq)：184-194
Viscosity (mPa.s/25°C): 11500-15000
Hydrolyzable Chloride (%): ≤0.10
Inorganic Chloride (ppm): ≤5
Volatile Content (%): ≤0.18
Color (APHA): ≤60
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：210-240
Softening point (℃)：14-23
Hydrolyzing chloride (%)：0.5
Inorganic chlorine (ppm)：100
Volatiles (%)：0.6
Color (Gardner method)：1.0
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：450-560
Softening point (℃)：60-76
Hydrolyzing chloride (%)：0.2
Inorganic chlorine (ppm)：100
Volatiles (%)：0.5
Color (Gardner method)：1.0
Brand:SINOCHEM HOLDINGS
Appearance：Solid, no mechanical impurities
Colour and lustre (Gardner)：2 the following
Epoxy equivalent (g/mol)：1750-2100
Viscosity at 25℃ (Gardner)：Y-Z1
Brand:SINOCHEM HOLDINGS
Appearance：Solid
Mechanical impurity：No
Color (Gardner)：2 Max(2)
Epoxy Equivalent (g/mol)：450-500
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appreance: Clear
Viscosity @23℃: 1300-1600 mPa.s
Solids content: 59-63 %
Gel time 80-140°C: 70-110 s
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min
Brand: AOC
Product family: Vinyl Ester Resin
Product type: Marine-Grade Vinyl Ester Resin
Application methods: Hand lay-up and spray-up
Curing system: MEK peroxide (MEKP) curing system
Certifications: Lloyd’s Register and RINA
Brand: AOC
Appearance: Clear
Solids content: 67 – 71 %
Viscosity @23℃:450-550 mPa.s
Gel time (25 until 35 ℃): 28-38min
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity @23℃:450-550 mPa.
Gel time at 25 ℃: Typical Value Base Gelcoat Brush：12-20min;Typical Value Base Gelcoat Spray:8-16 min
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value
Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)