Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 44 %
Density: 1.046 g/ml
Brand: SWANCOR
Appearance: Clear amber liquid
Solid Content: 58±1.5%
Viscosity: 380±100 cps
Gel Time: 15-25 min
HDT: 106-110°C
Barcol Hardness: 40±3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：35000-60000 mPa.s);（Typical Value Base Gelcoat Spray：21000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand: INEOS
Product type: Modified Vinyl Epoxy Resin / Marine Infusion Resin
Chemical nature: Modified Vinyl Epoxy Resin
Curing system: Thermosetting Resin System
Brand:Polylite
Appearance: Transparent light brownish-yellow liquid
Viscosity: 0.25±0.10 Pa·s
Acid value: 10±3 mg KOH/g
Solids content: 55±3%
Gel time: 25±5 min
Stability: 3 months in a dark place
Brand: Aliancys (Neogel)
Type: Air-drying repair gelcoat
Gel time at 25℃: TM 2245: 8-15 minutes
Coating thickness: not less than 0.3-0.5 mm
MEKP hardener dosage: 1%-2% (50% solution)
Brand：AOC
Appearance：Hazy
Viscosity, 23°C：200 – 700 mPa.s
Gel time from 25 to 35°C：14 – 45 minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):（Typical Value Base Gelcoat Spray：42500-52000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand：AOC
Appearance：clear
Viscosity, 23°C：260 – 300 mPa.s
Solids content, IR：64.0 – 67.0%
Gel time from 25 to 35°C：42 – 47 minutes
Cure time from 25°C to peak：52-56 minutes
Peak temperature：120 – 150 °C
Brand：Sika
Aspect：liquid
Colour：light amber
Viscosity at 25°C (mPa.s)：15
Density at 25°C：0.95
Brand：Sika
Aspect：liquid
Colour：light amber
Viscosity at 25°C (mPa.s)：1100
Density at 25°C：1.16
Brand:CCP
Appearance：Liquid
Equivalent WPE：185-195
Color, Max Gardner：≦50（APHA）Max
Specific Gravity（25℃）：1.15-1.18
Viscosity（25℃ Gardner）：11000-15000
Brand:CCP
Appearance：Liquid
Equivalent WPE：185-195
Color, Max Gardner：≦50（APHA）Max
Specific Gravity（25℃）：1.15-1.18
Viscosity（25℃ Gardner）：11000-15000
Brand:KUODO
EEW(g/eq):184-190
Viscosity(cps at 25°C):11,500-13,50
Hy-Cl(wt.%):0.05 max.
Specific Gravity*1(20°C):1.1
Brand:SANMU
Appearance：Transparent liquid, free of visible mechanical impurities
Epoxy equivalent (g / eq)：184-194
Viscosity (mPa.s/25°C): 11500-15000
Hydrolyzable Chloride (%): ≤0.10
Inorganic Chloride (ppm): ≤5
Volatile Content (%): ≤0.18
Color (APHA): ≤60
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：210-240
Softening point (℃)：14-23
Hydrolyzing chloride (%)：0.5
Inorganic chlorine (ppm)：100
Volatiles (%)：0.6
Color (Gardner method)：1.0
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：450-560
Softening point (℃)：60-76
Hydrolyzing chloride (%)：0.2
Inorganic chlorine (ppm)：100
Volatiles (%)：0.5
Color (Gardner method)：1.0
Brand:SINOCHEM HOLDINGS
Appearance：Solid, no mechanical impurities
Colour and lustre (Gardner)：2 the following
Epoxy equivalent (g/mol)：1750-2100
Viscosity at 25℃ (Gardner)：Y-Z1
Brand:SINOCHEM HOLDINGS
Appearance：Solid
Mechanical impurity：No
Color (Gardner)：2 Max(2)
Epoxy Equivalent (g/mol)：450-500
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：210-230
Hydrolytic Chlorine (%)：0.05 Max
Inorg.Cl （mg/kg：50 Max
Volatile /150℃,40min (%)：0.60 Max
Softening Point (℃ )：14-23
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand:Dow
Epoxide Equivalent Weight (g/eq)：182 – 192
Epoxide Percentage (%)：22.4 – 23.6
Epoxide Group Content (mmol/kg)：5200 – 5500
Color (Platinum Cobalt)：75 Max.
Viscosity @ 25°C (mPa•s)：11000 – 14000
Hydrolyzable Chloride Content (ppm)：500 Max.
Shelf Life (Months)：24
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%