Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 44 %
Density: 1.046 g/ml
Brand: SWANCOR
Appearance: Clear amber liquid
Solid Content: 58±1.5%
Viscosity: 380±100 cps
Gel Time: 15-25 min
HDT: 106-110°C
Barcol Hardness: 40±3
Brand:Polylite
Appearance: Transparent light brownish-yellow liquid
Viscosity: 0.25±0.10 Pa·s
Acid value: 10±3 mg KOH/g
Solids content: 55±3%
Gel time: 25±5 min
Stability: 3 months in a dark place
Chemical Name: Bisphenol A
CAS No.: 80-05-7
Molecular Formula: C₁₅H₁₆O₂
Molecular Weight: 228.29 g/mol
Appearance: White crystalline solid / flakes
Melting Point: ~155–157 °C
Boiling Point: ~220 °C
Solubility: Slightly soluble in water, soluble in organic solvents
Purity: ≥ 99.5%
Chemical Name: tert-Butyl Catechol
CAS No.: 98-29-3
Molecular Formula: C₁₀H₁₄O₂
Molecular Weight: 166.22 g/mol
Appearance: White to light yellow crystalline solid
Melting Point: ~53–56 °C
Boiling Point: ~285 °C
Solubility: Soluble in organic solvents, slightly soluble in water
Chemical Name: Hydroquinone
CAS No.: 123-31-9
Molecular Formula: C₆H₆O₂
Molecular Weight: 110.11 g/mol
Appearance: White crystalline solid
Melting Point: ~172–174 °C
Boiling Point: ~285 °C (decomposes)
Solubility: Soluble in water and organic solvents
Purity: ≥ 99.0%
Chemical Name: Propylene Glycol
CAS No.: 57-55-6
Molecular Formula: C₃H₈O₂
Molecular Weight: 76.09 g/mol
Appearance: Colorless viscous liquid
Boiling Point: ~188 °C
Melting Point: ~-59 °C
Solubility: Miscible with water and organic solvents
Purity: ≥ 99.5%
Chemical Name: Diethylene Glycol
CAS No.: 111-46-6
Molecular Formula: C₄H₁₀O₃
Molecular Weight: 106.12 g/mol
Appearance: Colorless viscous liquid
Boiling Point: ~245 °C
Melting Point: ~-8 °C
Solubility: Miscible with water and organic solvents
Purity: ≥ 99.0%
Chemical Name: Ethylene Glycol
CAS No.: 107-21-1
Molecular Formula: C₂H₆O₂
Molecular Weight: 62.07 g/mol
Appearance: Colorless viscous liquid
Boiling Point: ~197 °C
Melting Point: ~-13 °C
Solubility: Miscible with water and many organic solvents
Purity: ≥ 99.5%
Formula : C₈H₄O₃
Appearance : White crystalline flakes / needles or molten liquid
Melting Point : 130–132 °C
Boiling Point : ~284 °C
Solubility : Hydrolyzes in water to form phthalic acid
Flash Point : ~152 °C (combustible)
Brand:Trigonox®
Chemical family:Organic peroxide
CAS number:3851-87-4
Molecular Weight:314.5
Assay:74.0-76.0 %
Brand:CCP
Appearance：Liquid
Equivalent WPE：185-195
Color, Max Gardner：≦50（APHA）Max
Specific Gravity（25℃）：1.15-1.18
Viscosity（25℃ Gardner）：11000-15000
Brand:SANMU
Appearance：Transparent liquid, free of visible mechanical impurities
Epoxy equivalent (g / eq)：184-194
Viscosity (mPa.s/25°C): 11500-15000
Hydrolyzable Chloride (%): ≤0.10
Inorganic Chloride (ppm): ≤5
Volatile Content (%): ≤0.18
Color (APHA): ≤60
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：210-240
Softening point (℃)：14-23
Hydrolyzing chloride (%)：0.5
Inorganic chlorine (ppm)：100
Volatiles (%)：0.6
Color (Gardner method)：1.0
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：450-560
Softening point (℃)：60-76
Hydrolyzing chloride (%)：0.2
Inorganic chlorine (ppm)：100
Volatiles (%)：0.5
Color (Gardner method)：1.0
Brand:SINOCHEM HOLDINGS
Appearance：Solid, no mechanical impurities
Colour and lustre (Gardner)：2 the following
Epoxy equivalent (g/mol)：1750-2100
Viscosity at 25℃ (Gardner)：Y-Z1
Brand:SINOCHEM HOLDINGS
Appearance：Solid
Mechanical impurity：No
Color (Gardner)：2 Max(2)
Epoxy Equivalent (g/mol)：450-500
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：210-230
Hydrolytic Chlorine (%)：0.05 Max
Inorg.Cl （mg/kg：50 Max
Volatile /150℃,40min (%)：0.60 Max
Softening Point (℃ )：14-23
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Density:1.2 kg/dm3 at ISO 2811
Geltime, 2% MEKP-50:3 hours
Complete hardening:72 hours
Shrinkage，linear：2%
Brand:Dow
Cloud point（°C）：64
HLB2：12.5
Pour Point（°C）：16
Appearance：Colorless to slightly yellow, clear to slightly hazy