Brand: SWANCOR
Appearance: Clear amber liquid
Solid Content: 58±1.5%
Viscosity: 380±100 cps
Gel Time: 15-25 min
HDT: 106-110°C
Barcol Hardness: 40±3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：35000-60000 mPa.s);（Typical Value Base Gelcoat Spray：21000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand:Polylite
Appearance: Transparent light brownish-yellow liquid
Viscosity: 0.25±0.10 Pa·s
Acid value: 10±3 mg KOH/g
Solids content: 55±3%
Gel time: 25±5 min
Stability: 3 months in a dark place
Brand: Aliancys (Neogel)
Type: Air-drying repair gelcoat
Gel time at 25℃: TM 2245: 8-15 minutes
Coating thickness: not less than 0.3-0.5 mm
MEKP hardener dosage: 1%-2% (50% solution)
Brand：AOC
Appearance：Hazy
Viscosity, 23°C：200 – 700 mPa.s
Gel time from 25 to 35°C：14 – 45 minutes
Brand:KUODO
EEW(g/eq):184-190
Viscosity(cps at 25°C):11,500-13,50
Hy-Cl(wt.%):0.05 max.
Specific Gravity*1(20°C):1.1
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand:Dow
Epoxide Equivalent Weight (g/eq)：182 – 192
Epoxide Percentage (%)：22.4 – 23.6
Epoxide Group Content (mmol/kg)：5200 – 5500
Color (Platinum Cobalt)：75 Max.
Viscosity @ 25°C (mPa•s)：11000 – 14000
Hydrolyzable Chloride Content (ppm)：500 Max.
Shelf Life (Months)：24
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006