Brand: AOC
Appearance:Clear
Solids content, IR drying:55-63%
Viscosity @23℃:1100-1400 mPa.s
Gel_Time (25 until 35℃):9-15 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: AOC
Appreance: Clear-Slight hazy
Viscosity @23℃: 1700-2300 mPa.s
Solids content: 33-35 %
Product type: SMC/BMC resin
Grade: Palapreg® H 856-902
Processing methods: SMC and BMC molding
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Chemical nature: Pre-accelerated unsaturated polyester resin dissolved in styrene
Reactivity: Medium
Viscosity: Low
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: AOC
Product family: Gelcoat
Product type: Pre-accelerated spray gelcoat
Grade: Neogel® 8366-W-0100
Application method: Conventional spray or airless spray
Curing system: Standard MEKP, such as Butanox® M-50 or equivalent
Key features: High gloss, high elongation at break, excellent styrene resistance, easy application and repair, excellent spray properties, cures without foaming or microporosity
Brand:NanYa
Physical State:Solid particles
Epoxy Equivalent Weight (g/eq):200~220
Hydrolyzable chlorine(ppm):500
Brand:NanYa
Epoxy Equivalent Weight (g/eq): 184～190
Color (Gardner) :1.0max
Flash Point (℃) :150↑
Viscosity(cps，at 25 ℃) :12000～15000
Hydrolyzabie chlorine (ppm) :1000↓
Density (g/cm3 25℃) :1.16
Brand:NanYa
Epoxy Equivalent Weight (g/eq): 176～184
Hydrolyzable chlorine（ ppm）:1000↓
Color（Gardner）：0.0~1.0
Viscosity(cps，at 25 ℃) :8000～11000
Brand:NanYa
Epoxy Equivalent Weight (g/eq): 176～184
Hydrolyzable chlorine（ ppm）:300↓
Color（Gardner）：0.0~1.0
Viscosity(cps，at 25 ℃) :8000～11000
Brand:NanYa
Epoxy Equivalent Weight (g/eq): 450～500
Color (Gardner)：1.0max
Flash Point (℃)：200↑
Softening point ( 25 ℃)：64～74
Solution viscosity ( at 25 ℃)：D～F
Density (g/cm3 25℃):1.18
Brand:NanYa
Physical State:Liquid
Epoxy Equivalent Weight (g/eq): 450～500
Color (Gardner)：1.0max
Viscosity (cps，at 25 ℃):8000～15000
Non-volatility (%):74～76
Density (g/cm3 25℃):1.10
Brand:NanYa
Physical State:Solid
Epoxy Equivalent Weight (g/eq):380～410
Soften point:64～74 ℃
Hydrolyzable chlorine(PPM):200 max
Br content:46～50%
Color (Gardner)：1.0max
Brand:NanYa
Physical State:Semi Solid
Epoxy Equivalent Weight (g/eq):170～190
Color (Gardner)：3.0max
Solution viscosity *(25℃):H～J
Brand:SWANCOR
Appearance ：amber, clear liquid
Viscosity ：100-300 cps
Gel time ：15～35 min.
Shelf life ：6 months
Brand:SWANCOR
Appearance: Clear yellowish liquid
Solid Content(%)：67 ± 1
Specific Gravity：1.10 ± 0.02
Gel Time (min)：20-30
Shelf Life(months)：6(25℃)
Brand:SWANCOR
Appearance: Clear Amber Liquid
Solid Content (%):54~56
Viscosity (cps) *1：150~250
Gel Time (min) *2:15~25*2
Shelf Life (months/25oC):6
Brand:SWANCOR
Appearance: Clear yellowish liquid
Solid Content(%)：55±1
Viscosity (cps) *1：350±100
Specific Gravity：1.04±0.01
Gel Time (min)：15～25*²
Shelf Life(months)：9(25℃)
Brand:SWANCOR
Appearance: Clear yellow liquid
Solid Content(%)：73.5~69.5
Specific Gravity：1.08~1.12 g/cm3
Gel Time (min)：25~35
Shelf Life(months)：6
Brand: SWANCOR®
Product family: Auxiliary Agent
Product type: Resin promoter / accelerator
Grade: SWANCOR 1305
Key features: Controlled curing, good low-temperature performance, humidity resistance
Main applications: FRP resin curing systems
Brand:SWANCOR
Appearance:Turbid liquid
Density:1.09~1.10 g/cm3
Solid Content:54~60%
Viscosity*2:280~420cps
Acid Value：7-13 mgKOH/g
Stability at 80℃：≧24 hours
Brand:SWANCOR
Surface：Transparent liquid
Flash point：32℃
Dynamic 32℃ viscosity：＜ 20cps（ 25℃)
Solid＜ 20cps（ 25℃) content：6±2%
Brand:SWANCOR
Appearance:Brown translucent layered fluid
Gel time：20-30min
Suitable substrate:iron
Bonding strength：ASTMD1002， test rate:5mm/min
Iron:130kg/㎡