Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: COVESTRO
NCO content：19.6 ± 0.3 %
Non-volatile content2.2 g / 120 min / 100 °C：90 ± 1 %
Viscosity (23 °C)：500 ± 150 mPa·s
Color value (Iod)：≤ 40
Monomeric HDI：< 0.15%
Brand: COVESTRO
NCO content：13.3 ± 0.4 %
Non-volatile content2.2 g / 120 min / 100 °C：75 ± 1 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 40
Monomeric content：< 0.38%
Brand: COVESTRO
NCO content：16.5 ± 0.3 %
Non-volatile content2.2 g / 120 min / 100 °C：75 ± 1 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 40
Monomeric content：< 0.38%
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 50 g/l
Brand: COVESTRO
NCO content：4.4 ± 0.2 %
Viscosity (23 °C)：7000 ± 1000 mPa·s
Monomeric HDI：< 0.5%
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 120 g/l
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 50 g/l
Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Chemical nature: Pre-accelerated unsaturated polyester resin dissolved in styrene
Reactivity: Medium
Viscosity: Low
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: Henkel
Technology:Mold Release
Appearance：Clear, colorlessLMS
Chemical Type：Solvent Based Polymer
Odor：Solven
Cure：Room temperature cure
Cured Thermal Stability：≤400 °C
Application：Mold Sealer
Application Temperature：20 to 60 °C
Specific Benefit：
● No contaminating transfer
● High thermal stability
● Seals mold porosity, scratches or imperfections
Brand: Henkel
Technology:Silicone
Chemical Type:Oxime silicone
Appearance:Black pasteLMS
Components:One component -requires no mixing
Viscosity:Thixotropic paste
Cure：Room temperature vulcanizing (RTV)
Application:Sealing
Specific Benefits:Excellent resistance to automotive engine oils.
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:White or light creme suspensionLMS
Odor:Hydrocarbon
Cure：Room temperature cure
Cured Thermal Stability:≤280 °C
Application:Release Coatings
Application Temperature:15 to 35 °C
Specific Benefit:
● High gloss finish
● Multiple releases
● Minimal mold build-up
● Easy application
● Low odor
● Visible mold coverage
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:13 to 135 °C
Brand: Henkel
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:20 to 60 °C
Specific Benefit:
● Fast drying
● Non-contaminating transfer
● High thermal stability
● Non-CFC
● No mold build-up
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:20 to 60 °C
Specific Benefit:
● Fast drying
● Non-contaminating transfer
● High thermal stability
● Non-CFC
● No mold build-up
Brand: Henkel
Chemical Type: Epoxy
Appearance (Resin):White liquidLMS
Appearance (Hardener)：Gray liquidLMS
Components：Two component – requires mixing
Mix Ratio, by volume -Resin : Hardener：2 : 1
Mix Ratio, by weight -Resin : Hardener：100:50
Cure:Room temperature cure
Application：Bonding
Brand: Henkel
Technology:Acrylic
Chemical Type: Urethane methacrylate
Appearance (uncured):Green liquidLMS
Fluorescence：Positive under UV lightLMS
Components：One component- requires no mixing
Viscosity：Low
Cure: Anaerobic
Secondary Cure:Activator
Application：Retaining
Strength: High