Brand: INEOS
Density:80g/cm<sup>3</sup>
Flash point：38 ℃
Main application: FRP gel coat repair, topcoat preparation, fiberglass surface refinishing
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a
Brand: INEOS
Cone and Plate Viscosity：100 posie
Geltime：9 min
Product type: Polymer resin-based in-mold coating / FRP surface protection coating
Grade: Enguard AIDA
Main application: FRP in-mold coating, casting polymer surface protection, gelcoat surface finishing
Brand: INEOS
Properties at 23 °C
Viscosity, Brookfield RV5, 10 rpm: 7000 mPas ISO 2555
Viscosity, cone&plate: 250 mPas ISO 2884
Geltime, 2% MEKP-50: 7 min ASTM D2471
Brand: INEOS
Dynamic Viscosity: 325 mPa·s (cps)
Kinematic Viscosity: 300 cSt
Styrene Content: 33 %
Density: 1.08 g/ml
Brand: COVESTRO
Form supplied：approx. 60 % in butyl acetate
NCO content：10.5 ± 0.5 %
Non-volatile content：60.0 ± 2.0 %
Viscosity (23 °C)：2,200 ± 1,000 mPa·s
Iodine color value：≤ 4
Monomeric TDI + HDI：< 0.5%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：7.4 ± 0.2 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.50%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：7.4 ± 0.2 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.50%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：8.0 ± 0.3 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：1,300 ± 450 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.10%
Brand: CHEM TREND
Product family: Mold Release Agents / Auxiliary Agents
Product type: Solvent-Based Semi-Permanent Mold Release Agent
Grade: Chemlease® 1365 EZ
Chemical nature: Solvent-Based Semi-Permanent Release Coating
Product form: Liquid mold release agent
Application methods: Wipe-on application using clean cotton cloths
Brand: CHEM TREND
Grade: Chemlease® PMR-90 EZ
Chemical nature: Solvent-Based Semi-Permanent Release Coating
Product form: Liquid mold release agent
Application methods: Wipe-on application using clean cotton cloths
Brand: EVONIK
Molecular weight：7000 g/mol
Glass transition temperature (solid)：-5 ℃
Density (20 ) (solution):1.10 g/ cm
Flash point：72 ℃
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):270 – 330 m²/g
tamped density:Approx. 50 g/l
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 50 g/l
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Wax Melting or Softening Point: 195 – 210°F (88 – 99°C)
Penetration Hardness: 1 at 25°C (carnauba wax)
Color: light blue tint (color coded for identification)
VOC Content: 4.84lbs./gal (580g/l)
Brand: AOC
Geltime at 25℃ (2ml Butanox M50):10-16 minutes
Peak temperature: 175-190 ℃
Viscosity at 25℃ (#4, rpm2): 30000-36000 mPa.s
Viscosity at 25℃ (#4, rpm20): 4000-5500 mPa.s
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: INEOS
Properties at 23 °C
Viscosity, Brookfield RV5, 10 rpm: 7000 mPas ISO 2555
Viscosity, cone&plate: 250 mPas ISO 2884
Geltime, 2% MEKP-50: 7 min ASTM D2471
Brand: AOC
Appearance: Hazy
Viscosity, 23℃: 620-680 mPa.s
Viscosity, 23℃: 590-630 mPa.s
Viscosity, 23℃: 530-560 mPa.s
Solids content, IR: 68-71 % TM 2033
Gel time 25 to 35℃: 38-42 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Appearance：Clear
Solids content, IR drying：64-68%
Viscosity @23℃：400-550
Gel_Time (25 until 35 °C)：12-25 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min