Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Density:80g/cm<sup>3</sup>
Flash point：38 ℃
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a
Brand: INEOS
Brookfield (RV4/10rpm):10 000 mPas at ISO 2555
Cone & Plate (ICI):300 mPas at ISO 2884
Styrene conten:< 35% at ISO 4864
gel time (2.0% MEKP-50):12 min
Brand: INEOS
Viscosity at 25°C:
Brookfield RVT sp3, 60rpm:385 mPas at ISO 2555
Brookfield RVT sp3, 6rpm:900 mPas at ISO 2555
Styrene Content:40% at SFS 4864
Index of thixotropy:2.33
Brand: INEOS
Property at 23 °C
Density:1.2 kg/dm3 at ISO 2811
Geltime, 2% MEKP-50:3 hours
Complete hardening:72 hours
Shrinkage，linear：2%
Brand: INEOS
Cone and Plate Viscosity：100 posie
Geltime：9 min
Brand:OXBOND
Chemical Type：Demoulding Wax
Brand:OXBOND
Chemical Type：Polishing Paste