Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 44 %
Density: 1.046 g/ml
Brand: SWANCOR
Appearance: Clear amber liquid
Solid Content: 58±1.5%
Viscosity: 380±100 cps
Gel Time: 15-25 min
HDT: 106-110°C
Barcol Hardness: 40±3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：35000-60000 mPa.s);（Typical Value Base Gelcoat Spray：21000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand: INEOS
Product type: Modified Vinyl Epoxy Resin / Marine Infusion Resin
Chemical nature: Modified Vinyl Epoxy Resin
Curing system: Thermosetting Resin System
Brand:Polylite
Appearance: Transparent light brownish-yellow liquid
Viscosity: 0.25±0.10 Pa·s
Acid value: 10±3 mg KOH/g
Solids content: 55±3%
Gel time: 25±5 min
Stability: 3 months in a dark place
Brand: Aliancys (Neogel)
Type: Air-drying repair gelcoat
Gel time at 25℃: TM 2245: 8-15 minutes
Coating thickness: not less than 0.3-0.5 mm
MEKP hardener dosage: 1%-2% (50% solution)
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Viscosity at 25°C:
Brookfield RVT sp3, 60rpm:385 mPas at ISO 2555
Brookfield RVT sp3, 6rpm:900 mPas at ISO 2555
Styrene Content:40% at SFS 4864
Index of thixotropy:2.33
Brand: INEOS
Dynamic Viscosity: 325 mPa·s (cps)
Kinematic Viscosity: 300 cSt
Styrene Content: 33 %
Density: 1.08 g/ml
Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 45 %
Density: 1.046 g/ml
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Appearance：Clear
Solids content, IR drying：64-68%
Viscosity @23℃：400-550
Gel_Time (25 until 35 °C)：12-25 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min
Brand: AOC
Product family: Vinyl Ester Resin
Product type: Marine-Grade Vinyl Ester Resin
Application methods: Hand lay-up and spray-up
Curing system: MEK peroxide (MEKP) curing system
Certifications: Lloyd’s Register and RINA
Brand: AOC
Appearance: Clear
Solids content: 67 – 71 %
Viscosity @23℃:450-550 mPa.s
Gel time (25 until 35 ℃): 28-38min
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity @23℃:450-550 mPa.
Gel time at 25 ℃: Typical Value Base Gelcoat Brush：12-20min;Typical Value Base Gelcoat Spray:8-16 min
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value
Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value
Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)