Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：35000-60000 mPa.s);（Typical Value Base Gelcoat Spray：21000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand: Aliancys (Neogel)
Type: Air-drying repair gelcoat
Gel time at 25℃: TM 2245: 8-15 minutes
Coating thickness: not less than 0.3-0.5 mm
MEKP hardener dosage: 1%-2% (50% solution)
Brand：AOC
Appearance：Hazy
Viscosity, 23°C：200 – 700 mPa.s
Gel time from 25 to 35°C：14 – 45 minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):（Typical Value Base Gelcoat Spray：42500-52000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand：AOC
Appearance：clear
Viscosity, 23°C：260 – 300 mPa.s
Solids content, IR：64.0 – 67.0%
Gel time from 25 to 35°C：42 – 47 minutes
Cure time from 25°C to peak：52-56 minutes
Peak temperature：120 – 150 °C
Brand: AOC
Geltime at 25℃ (2ml Butanox M50):10-16 minutes
Peak temperature: 175-190 ℃
Viscosity at 25℃ (#4, rpm2): 30000-36000 mPa.s
Viscosity at 25℃ (#4, rpm20): 4000-5500 mPa.s
Brand: AOC
Appearance: Hazy
Viscosity, 23℃: 620-680 mPa.s
Viscosity, 23℃: 590-630 mPa.s
Viscosity, 23℃: 530-560 mPa.s
Solids content, IR: 68-71 % TM 2033
Gel time 25 to 35℃: 38-42 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Appearance：Clear
Solids content, IR drying：64-68%
Viscosity @23℃：400-550
Gel_Time (25 until 35 °C)：12-25 min