Desmodur E 15

Fumed Silica / Thixotropic Agent

Brand: COVESTRO
NCO content：4.4 ± 0.2 %
Viscosity (23 °C)：7000 ± 1000 mPa·s
Monomeric HDI：< 0.5%

AEROSIL 200 V

Rheology Control Additive / Thixotropic Silica

Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO₂ content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 120 g/l

AEROSIL 200 F

Rheology Control Agent / Thickening Agent

Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO₂ content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 50 g/l

Neogel 8373-I-0000

Transparent ISO-NPG Gelcoat

Brand: AOC
Appearance: transparent thixotropic liquid
Viscosity at 25℃ (#4, rpm2):Typical Value：13500-18500 mPa.s
Viscosity at 25℃ (#4, rpm20):Typical Value：2350-3200 mPa.s
Gel time at 25 ℃: Typical Value：8-12 minute

Basisil- 200

Anti-Settling & Anti-Caking Additive

Brand: BASHAN
Specific Surface Area BET（m²/g）：200±15
pH Value in 4% dispersion:3.8～4.2
Loss on Drying 2h@ 105℃（％）:≤1.5
Loss on Ignition 2h@ 1000℃（％）:≤2.0
Sieve Residue 45μm（％）:≤0.05
Bulk Density （g/l）：40～60
SiO2Content（％）：≥99.8

Neogel 8373-W-8921

Water & Weather-Resistant Gelcoat

Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes

Neogel 8373-W-9118

Water & Weather-Resistant Gelcoat

VESTAMIN IPD

Cycloaliphatic Diamine Epoxy Hardener

Brand: EVONIK
Molecular weight C₁₀H₂₂N₂:170.3g/mol
Equivalent weight:85.2g/val
H-active equipment weight:42.6g/val
Density at 20℃：0.820-0.925gcm³

Neogel 8373-W-9315

NPG Marine UV Gelcoat

TT-196

General-Purpose UPR

Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67

Neogel 8373-W-9504

Water & Weather-Resistant Gelcoat

Neogel 8373-W-9512

NPG UV Gelcoat

TT-RP-126 promoter

Polyester Button Resin Promoter

Brand:Thousands Technology
Appearance: clear cyan purple liquid
Resin casting body color: light color , light blue, vivid color

TT-Promoter E

Room-Temperature Cure Promoter

Brand:Thousands Technology
Appearance: clear purple liquid
Gel time (25 ℃)：≤ 5 min
Density (25 ℃): 0.900-0.922g / min
Resin casting body color: original color

TT-Accelerator D

Light-Color UPR Accelerator

Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color

Neobond VE 6100-W-1

Vinyl Ester Structural Adhesive

Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes

TT-Promoter A2

Cobalt Accelerator / UPR Curing Promoter

Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color

Palatal P 65TV-959

Hand Lay-Up & Spray-Up Laminating Resin

Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min

PALATAL A400-972

Isophthalic Unsaturated Polyester Resin

Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min

TT-MIBKP-H

Unsaturated Polyester Resin Curing Initiator

Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s

PALATAL A400 TV-957 S

CCS-Certified Boat Building Laminating Resin

Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-250 mPa.s
Solids content, IR drying:52-58 %
Acid value:11-18 mg KOH/g
Gel time(25℃to35 °C):40-70 min

TT-DHBP-101-45S-PS

Silicone Rubber Crosslinking Agent

Brand:Thousands Technology
Appearance: White high viscous paste
Assay:44.0-46.0 %
Grade: DHBP-101-45S-PS
CAS No.: 78-63-7
Form: Paste
Peroxide concentration: 45%
Key function: Crosslinking agent for silicone rubber

TT-DMP-30

Epoxy Curing Accelerator

Brand:Thousands Technology
Appearance: Yellow viscous liquid
Amine value (mgKOH/g): 600–630
Color (Gardner): ≤ 6
Viscosity (25 °C, mPa·s): 100–300

TT-AGE

C12–14 Alkyl Glycidyl Ether

Brand:Thousands Technology
Appearance: colorless transparent liquid
Epoxy Equivalent Weight(g/eq):0.32
Viscosity(cps/25℃) 5-15mpas
Organic Chlorine（EQ/100g）:≤0.02
Inorganic Chlorine （EQ/100g）：≤0.005
Moisture Content(%):≤0.1

Industry

Desmodur E 15

AEROSIL 200 V

AEROSIL 200 F

Neogel 8373-I-0000

Basisil- 200

Neogel 8373-W-8921

Neogel 8373-W-9118

VESTAMIN IPD

Neogel 8373-W-9315

TT-196

Neogel 8373-W-9504

Neogel 8373-W-9512

TT-RP-126 promoter

TT-Promoter E

TT-Accelerator D

Neobond VE 6100-W-1

TT-Promoter A2

Palatal P 65TV-959

PALATAL A400-972

TT-MIBKP-H

PALATAL A400 TV-957 S

TT-DHBP-101-45S-PS

TT-DMP-30

TT-AGE

Return Conditions

Return Period

Refund Method

Exchange Policy

Industry

Desmodur E 15

AEROSIL 200 V

AEROSIL 200 F

Neogel 8373-I-0000

Basisil- 200

Neogel 8373-W-8921

Neogel 8373-W-9118

VESTAMIN IPD

Neogel 8373-W-9315

TT-196

Neogel 8373-W-9504

Neogel 8373-W-9512

TT-RP-126 promoter

TT-Promoter E

TT-Accelerator D

Neobond VE 6100-W-1

TT-Promoter A2

Palatal P 65TV-959

PALATAL A400-972

TT-MIBKP-H

PALATAL A400 TV-957 S

TT-DHBP-101-45S-PS

TT-DMP-30

TT-AGE