Brand:KUODO
EEW(g/eq):184-190
Viscosity(cps at 25°C):11,500-13,50
Hy-Cl(wt.%):0.05 max.
Specific Gravity*1(20°C):1.1
Brand:SANMU
Appearance：Transparent liquid, free of visible mechanical impurities
Epoxy equivalent (g / eq)：184-194
Viscosity (mPa.s/25°C): 11500-15000
Hydrolyzable Chloride (%): ≤0.10
Inorganic Chloride (ppm): ≤5
Volatile Content (%): ≤0.18
Color (APHA): ≤60
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：210-240
Softening point (℃)：14-23
Hydrolyzing chloride (%)：0.5
Inorganic chlorine (ppm)：100
Volatiles (%)：0.6
Color (Gardner method)：1.0
Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：450-560
Softening point (℃)：60-76
Hydrolyzing chloride (%)：0.2
Inorganic chlorine (ppm)：100
Volatiles (%)：0.5
Color (Gardner method)：1.0
Brand:SINOCHEM HOLDINGS
Appearance：Solid, no mechanical impurities
Colour and lustre (Gardner)：2 the following
Epoxy equivalent (g/mol)：1750-2100
Viscosity at 25℃ (Gardner)：Y-Z1
Brand:SINOCHEM HOLDINGS
Appearance：Solid
Mechanical impurity：No
Color (Gardner)：2 Max(2)
Epoxy Equivalent (g/mol)：450-500
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：210-230
Hydrolytic Chlorine (%)：0.05 Max
Inorg.Cl （mg/kg：50 Max
Volatile /150℃,40min (%)：0.60 Max
Softening Point (℃ )：14-23
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand:Dow
Epoxide Equivalent Weight (g/eq)：182 – 192
Epoxide Percentage (%)：22.4 – 23.6
Epoxide Group Content (mmol/kg)：5200 – 5500
Color (Platinum Cobalt)：75 Max.
Viscosity @ 25°C (mPa•s)：11000 – 14000
Hydrolyzable Chloride Content (ppm)：500 Max.
Shelf Life (Months)：24
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Density:80g/cm<sup>3</sup>
Flash point：38 ℃
Main application: FRP gel coat repair, topcoat preparation, fiberglass surface refinishing
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a
Brand: INEOS
Viscosity at 25°C:
Brookfield RVT sp3, 60rpm:385 mPas at ISO 2555
Brookfield RVT sp3, 6rpm:900 mPas at ISO 2555
Styrene Content:40% at SFS 4864
Index of thixotropy:2.33
Brand: INEOS
Property at 23 °C
Density:1.2 kg/dm3 at ISO 2811
Geltime, 2% MEKP-50:3 hours
Complete hardening:72 hours
Shrinkage，linear：2%
Brand: INEOS
Cone and Plate Viscosity：100 posie
Geltime：9 min
Product type: Polymer resin-based in-mold coating / FRP surface protection coating
Grade: Enguard AIDA
Main application: FRP in-mold coating, casting polymer surface protection, gelcoat surface finishing
Brand:OXBOND
Product family: Mold Release Agents / Composite Auxiliary Agents
Product type: Multiple-Release Paste Demoulding Wax
Chemical nature: Synthetic wax and high-temperature resin blend with pure carnauba wax base
Product form: Paste wax
Brand:OXBOND
Product family: Mold Polishing & Composite Finishing Auxiliary Agents
Product type: Wax-blend polishing paste / Machine glaze compound
Grade: OXBOND N3 Polishing Paste
Main application: FRP mold polishing, composite surface finishing, high-gloss restoration
Brand:OXBOND
Product type: High-Temperature Demolding Wax
Chemical nature: Refined Carnauba Wax blended with high-temperature synthetic ingredients and petroleum distillates
Product form: Paste release wax
Brand:OXBOND
Chemical Type：Release Wax
Product form: Paste wax
Main functions: Mold release, surface gloss enhancement, repeated demolding support and FRP mold protection
Brand:OXBOND
Chemical Type：Polishing Paste
Chemical nature: Special wax blend polishing paste designed for composite materials
Product form: Polishing paste
Main functions: Surface polishing, defect removal, brightness enhancement and FRP mold maintenance
Brand:HUNTSMAN
Appearance：Colorless to pale yellow with slight haze
Color, Pt-Co：50 max.
Primary amine, % of total amine：90 min.
Total acetylatables, meq/g：6.5 – 7.1
Total amine, meq/g：6.1 – 6.6
Water, wt%：0.25 max.
Brand:HUNTSMAN
Appearance：Colorless to pale yellow liquid ST-30.1 with slight haze permitted
Color, Pt-Co：25 max.
Primary amine, % of total amine：97 min.
Total acetylatables, meq/g：8.3 – 9.1
Total amine, % acetylatables：94.0 min.
Water, wt%：0.20 max.