Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Density:1.2 kg/dm3 at ISO 2811
Geltime, 2% MEKP-50:3 hours
Complete hardening:72 hours
Shrinkage，linear：2%
Brand:Dow
Cloud point（°C）：64
HLB2：12.5
Pour Point（°C）：16
Appearance：Colorless to slightly yellow, clear to slightly hazy
Brand: INEOS
Dynamic Viscosity: 325 mPa·s (cps)
Kinematic Viscosity: 300 cSt
Styrene Content: 33 %
Density: 1.08 g/ml
Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 45 %
Density: 1.046 g/ml
Brand: COVESTRO
Form supplied：approx. 60 % in butyl acetate
NCO content：10.5 ± 0.5 %
Non-volatile content：60.0 ± 2.0 %
Viscosity (23 °C)：2,200 ± 1,000 mPa·s
Iodine color value：≤ 4
Monomeric TDI + HDI：< 0.5%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：7.4 ± 0.2 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.50%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：7.4 ± 0.2 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.50%
Brand: COVESTRO
Form supplied：approx. 51 % in butyl acetate
NCO content：8.0 ± 0.3 %
Non-volatile content(0.2 g / 60 min / 120°C)：51.0 ± 2.0 %
Viscosity (23 °C)：1,300 ± 450 mPa·s
Color value (Iod)：≤ 1.0
Monomeric content：< 0.10%