Brand: EVONIK
carbon content：2.0 – 4.0%
loss on drying*2 hours at 105 °C：≤0.5 %
pH value in 4% dispersion:≥5.5
SiO2 content：>99.8 %
specific surfacearea(BET):135 – 185 m²/g
Brand: EVONIK
carbon content：0.7 – 1.3%
loss on drying*2 hours at 105 °C：≤0.5 %
pH value in 4% dispersion:3.7 – 4.7
SiO2 content：>99.8 %
specific surfacearea(BET):150 – 190 m²/g
Brand:Deawa
Appearance: Clear liquid
Odor: Hydrocarbon
Solvent: Polysiloxane/Fluororesin/hydrocarbon
Relative Density: 0.732 (+/-0.02)
Flash Point: 26℃
Shelf Life: 1 year
Cured Thermal Stability: ≤ 330℃（≤626°F）
Application Temperature: 13 to 135℃（55 to 275°F）
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Wax Melting or Softening Point: 195 – 210°F (88 – 99°C)
Penetration Hardness: 1 at 25°C (carnauba wax)
Color: light blue tint (color coded for identification)
VOC Content: 4.84lbs./gal (580g/l)
Brand:Ketjenblack®
Chemical family:Electroconductive carbon black
CAS number:1333-86-4
Physical form:Pellets
Chemical name:Electroconductive carbon black
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: Ineos
Properties at 23 °C
Viscosity, Brookfield RV5, 10 rpm: 7000 mPas ISO 2555
Viscosity, cone&plate: 250 mPas ISO 2884
Geltime, 2% MEKP-50: 7 min ASTM D2471
Brand:Nouryon
Apparent bulk density：100-120 kg/m³
Appearance：Black free-flowing pellets
Ash：≤0.1 %
Fines <125 micron: ≤7 %
Grit content: ≤30 mg/kg
Iodine absorption :1000-1100 mg/g
Moisture: ≤0.5 %
pH: 9.0-10.5
Pore volume, DBP: 480-510 ml/100g
Volatiles: ≤1.0 %
Brand:Deawa
Appearance: Clear liquid
Odor: Hydrocarbon odor
Solvent: Aliphatic hydrocarbons
Specific gravity: 0.760±0.010
Thermal stability after curing: 400°C
Brand: COVESTRO
NCO content：19.6 ± 0.3 %
Non-volatile content2.2 g / 120 min / 100 °C：90 ± 1 %
Viscosity (23 °C)：500 ± 150 mPa·s
Color value (Iod)：≤ 40
Monomeric HDI：< 0.15%
Brand: COVESTRO
NCO content：13.3 ± 0.4 %
Non-volatile content2.2 g / 120 min / 100 °C：75 ± 1 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 40
Monomeric content：< 0.38%
Brand: COVESTRO
NCO content：16.5 ± 0.3 %
Non-volatile content2.2 g / 120 min / 100 °C：75 ± 1 %
Viscosity (23 °C)：250 ± 75 mPa·s
Color value (Iod)：≤ 40
Monomeric content：< 0.38%
Brand: COVESTRO
NCO content：4.4 ± 0.2 %
Viscosity (23 °C)：7000 ± 1000 mPa·s
Monomeric HDI：< 0.5%
Brand: EVONIK
Molecular weight C10H22N2:170.3g/mol
Equivalent weight:85.2g/val
H-active equipment weight:42.6g/val
Density at 20℃：0.820-0.925gcm3
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand:Thousands Technology
Appearance: White high viscous paste
Assay:44.0-46.0 %
Grade: DHBP-101-45S-PS
CAS No.: 78-63-7
Form: Paste
Peroxide concentration: 45%
Key function: Crosslinking agent for silicone rubber
Brand:Thousands Technology
Appearance: Yellow viscous liquid
Amine value (mgKOH/g): 600–630
Color (Gardner): ≤ 6
Viscosity (25 °C, mPa·s): 100–300
Brand:Thousands Technology
Appearance: colorless transparent liquid
Epoxy Equivalent Weight(g/eq):0.32
Viscosity(cps/25℃) 5-15mpas
Organic Chlorine（EQ/100g）:≤0.02
Inorganic Chlorine （EQ/100g）：≤0.005
Moisture Content(%):≤0.1
Brand:Thousands Technology
Appearance：light yellow liquid
Viscosity(25 °C): 20-80mPa.s
Acid value:660min mgKOH/g
Free acid:0.5max%
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance:Clear
Solids content, IR drying:55-63%
Viscosity @23℃:1100-1400 mPa.s
Gel_Time (25 until 35℃):9-15 min