Brand: PALATAL® (AOC)
Product family: Unsaturated Polyester Resins / Orthophthalic Polyester Resins
Product type: Pre-accelerated, Thixotropic Unsaturated Polyester Laminating Resin
Grade: PALATAL® P61TV-956
Chemical nature: Orthophthalic Polyester Resin Based on Orthophthalic Acid and Standard Glycols in Styrene
Brand：AOC
Appearance：Hazy
Viscosity, 23°C：200 – 700 mPa.s
Gel time from 25 to 35°C：14 – 45 minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):（Typical Value Base Gelcoat Spray：42500-52000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：5700-7300 mPa.s);（Typical Value Base Gelcoat Spray：3500-5200 mPa.s)
Gel time at 25 ℃: (Typical ValueBase Gelcoat Brush：12-18 minutes);（Typical Value Base Gelcoat Spray：8-15 minutes)
Brand：AOC
Appearance：clear
Viscosity, 23°C：260 – 300 mPa.s
Solids content, IR：64.0 – 67.0%
Gel time from 25 to 35°C：42 – 47 minutes
Cure time from 25°C to peak：52-56 minutes
Peak temperature：120 – 150 °C
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a
Brand: AOC
Appearance: Hazy
Viscosity, 23℃: 620-680 mPa.s
Viscosity, 23℃: 590-630 mPa.s
Viscosity, 23℃: 530-560 mPa.s
Solids content, IR: 68-71 % TM 2033
Gel time 25 to 35℃: 38-42 min
Brand: AOC
Appreance: Clear
Viscosity @23℃: 1300-1600 mPa.s
Solids content: 59-63 %
Gel time 80-140°C: 70-110 s
Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67
Brand: AOC
Appreance: Clear-Slight hazy
Viscosity @23℃: 1700-2300 mPa.s
Solids content: 33-35 %
Product type: SMC/BMC resin
Grade: Palapreg® H 856-902
Processing methods: SMC and BMC molding
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Chemical nature: Pre-accelerated unsaturated polyester resin dissolved in styrene
Reactivity: Medium
Viscosity: Low
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:20-26mgKOH/g
Viscosity，25℃:0.7-0.8Pa.s
Solid Content:62-68%
Thermal Stability,80℃:≥24
Gel time:6-18
Brand:Polylite
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:14-22 mg KOH/g
Viscosity, 25℃:1.6-2.3 Pa.s
Solid Content:70-76 %
Gel Time, 25℃:8.5-10.5 min
Thermal Stability, 80℃:≥24h
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:14-20mgKOH/g
Viscosity，25℃:0.14-0.16Pa.s
Solid Content:52-58%
Gel time:25-38min
Brand:Polylite
Appearance:pink liquid
Acid Value：17-24mgKOH/g
Viscosity，25℃：0.3-0.4 Pa.s
Solid Content：58-64%
Gel time：25-43min
Brand:Polylite
Appearance: Light yellow ransparent viscous liquid
Acid Value: 19-25mgKOH/g
Viscosity，25℃: 0.30-0.60Pa.s
Solid Content: 59-65%
Gelation time,25℃: 6-18
Brand:Polylite
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Brand:Polylite
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.65-0.75 Pa.s
Solid Content:63-69 %
Thermal Stability,80℃:≥24 h
Gel Time:4.5-9.5 min