Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance:Clear
Solids content, IR drying:55-63%
Viscosity @23℃:1100-1400 mPa.s
Gel_Time (25 until 35℃):9-15 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: Henkel
Chemical Type: Epoxy
Appearance (Mixed):Steel Colored Paste
Mix Ratio, by volume -Resin : Hardener|：1:1
Mix Ratio, by weight -Resin : Hardener：100 : 56.5
Cure:Room temperature cure after mixing
Application：North America – Metal Repair
Specific Benefit：
● Hardens in ten minutes
● Non sagging
● Steel filled system – cures to metal-like finish
● Bonds to steel, cast iron,stainless steel, concrete,copper, aluminum, and clean and abraded bronze
Brand: Henkel
Technology:Mold Release
Appearance：Clear, colorlessLMS
Chemical Type：Solvent Based Polymer
Odor：Solven
Cure：Room temperature cure
Cured Thermal Stability：≤400 °C
Application：Mold Sealer
Application Temperature：20 to 60 °C
Specific Benefit：
● No contaminating transfer
● High thermal stability
● Seals mold porosity, scratches or imperfections