Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-250 mPa.s
Solids content, IR drying:52-58 %
Acid value:11-18 mg KOH/g
Gel time(25℃to35 °C):40-70 min
Brand:Thousands Technology
Appearance: White high viscous paste
Assay:44.0-46.0 %
Grade: DHBP-101-45S-PS
CAS No.: 78-63-7
Form: Paste
Peroxide concentration: 45%
Key function: Crosslinking agent for silicone rubber
Brand:Thousands Technology
Appearance: Yellow viscous liquid
Amine value (mgKOH/g): 600–630
Color (Gardner): ≤ 6
Viscosity (25 °C, mPa·s): 100–300
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: Beige
Viscosity @23℃（20S-1）:670-870 mPa.s
Viscosity @23℃（50S-1）：600-680 mPa.s
Viscosity @23℃（250S-1）：520-580 mPa.s
Solids content, IR drying：74.5-77.5 %
Gel_Time (25 until 35℃):9-11 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance:Clear
Solids content, IR drying:55-63%
Viscosity @23℃:1100-1400 mPa.s
Gel_Time (25 until 35℃):9-15 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Chemical nature: Pre-accelerated unsaturated polyester resin dissolved in styrene
Reactivity: Medium
Viscosity: Low
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: AOC
Product family: Gelcoat
Product type: Pre-accelerated spray gelcoat
Grade: Neogel® 8366-W-0100
Application method: Conventional spray or airless spray
Curing system: Standard MEKP, such as Butanox® M-50 or equivalent
Key features: High gloss, high elongation at break, excellent styrene resistance, easy application and repair, excellent spray properties, cures without foaming or microporosity
Brand: Henkel
Chemical Type: Epoxy
Appearance (Mixed):Steel Colored Paste
Mix Ratio, by volume -Resin : Hardener|：1:1
Mix Ratio, by weight -Resin : Hardener：100 : 56.5
Cure:Room temperature cure after mixing
Application：North America – Metal Repair
Specific Benefit：
● Hardens in ten minutes
● Non sagging
● Steel filled system – cures to metal-like finish
● Bonds to steel, cast iron,stainless steel, concrete,copper, aluminum, and clean and abraded bronze
Brand: Henkel
Technology:Mold Release
Appearance：Clear, colorlessLMS
Chemical Type：Solvent Based Polymer
Odor：Solven
Cure：Room temperature cure
Cured Thermal Stability：≤400 °C
Application：Mold Sealer
Application Temperature：20 to 60 °C
Specific Benefit：
● No contaminating transfer
● High thermal stability
● Seals mold porosity, scratches or imperfections
Brand: Henkel
Technology:Epoxy Resin
Additional Information:2-component solvent free toughend epoxy resin
Product type: Two-component epoxy structural adhesive
Grade: TEROSON® EP 5055
Chemical nature: Epoxy resin (Part A) + amine hardener (Part B)
Mixing ratio A:B: 1:1 by volume