Brand:SANMU
Appearance：transparent solid
Epoxy equivalent (g / eq)：450-560
Softening point (℃)：60-76
Hydrolyzing chloride (%)：0.2
Inorganic chlorine (ppm)：100
Volatiles (%)：0.5
Color (Gardner method)：1.0
Brand:SINOCHEM HOLDINGS
Appearance：Solid, no mechanical impurities
Colour and lustre (Gardner)：2 the following
Epoxy equivalent (g/mol)：1750-2100
Viscosity at 25℃ (Gardner)：Y-Z1
Brand:SINOCHEM HOLDINGS
Appearance：Solid
Mechanical impurity：No
Color (Gardner)：2 Max(2)
Epoxy Equivalent (g/mol)：450-500
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：210-230
Hydrolytic Chlorine (%)：0.05 Max
Inorg.Cl （mg/kg：50 Max
Volatile /150℃,40min (%)：0.60 Max
Softening Point (℃ )：14-23
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：175～185
Inorganic Chlorine (mg/kg)：50 Max
Hydrolytic Chlorine (%)：0.050 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：8000～11000
Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand:Dow
Epoxide Equivalent Weight (g/eq)：182 – 192
Epoxide Percentage (%)：22.4 – 23.6
Epoxide Group Content (mmol/kg)：5200 – 5500
Color (Platinum Cobalt)：75 Max.
Viscosity @ 25°C (mPa•s)：11000 – 14000
Hydrolyzable Chloride Content (ppm)：500 Max.
Shelf Life (Months)：24
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Density:80g/cm<sup>3</sup>
Flash point：38 ℃
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a