Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-250 mPa.s
Solids content, IR drying:52-58 %
Acid value:11-18 mg KOH/g
Gel time(25℃to35 °C):40-70 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-230 mPa.s
Solids content, IR drying：61-63 %
Acid value:16.5-23.5 mgKOH/g
Gel time(25℃to35 °C):22-40 min
Brand: AOC
Appearance: Beige
Viscosity @23℃（20S-1）:670-870 mPa.s
Viscosity @23℃（50S-1）：600-680 mPa.s
Viscosity @23℃（250S-1）：520-580 mPa.s
Solids content, IR drying：74.5-77.5 %
Gel_Time (25 until 35℃):9-11 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s