Brand: AOC
Appearance: transparent thixotropic liquid
Viscosity at 25℃ (#4, rpm2):Typical Value：13500-18500 mPa.s
Viscosity at 25℃ (#4, rpm20):Typical Value：2350-3200 mPa.s
Gel time at 25 ℃: Typical Value：8-12 minute
Brand: BASHAN
Specific Surface Area BET（m²/g）：200±15
pH Value in 4% dispersion:3.8～4.2
Loss on Drying 2h@ 105℃（％）:≤1.5
Loss on Ignition 2h@ 1000℃（％）:≤2.0
Sieve Residue 45μm（％）:≤0.05
Bulk Density （g/l）：40～60
SiO2Content（％）：≥99.8
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: EVONIK
Molecular weight C10H22N2:170.3g/mol
Equivalent weight:85.2g/val
H-active equipment weight:42.6g/val
Density at 20℃：0.820-0.925gcm3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand:Thousands Technology
Appearance: clear cyan purple liquid
Resin casting body color: light color , light blue, vivid color
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time (25 ℃)：≤ 5 min
Density (25 ℃): 0.900-0.922g / min
Resin casting body color: original color
Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s
Brand:Thousands Technology
Appearance: Yellow viscous liquid
Amine value (mgKOH/g): 600–630
Color (Gardner): ≤ 6
Viscosity (25 °C, mPa·s): 100–300
Brand:Thousands Technology
Appearance: colorless transparent liquid
Epoxy Equivalent Weight(g/eq):0.32
Viscosity(cps/25℃) 5-15mpas
Organic Chlorine（EQ/100g）:≤0.02
Inorganic Chlorine （EQ/100g）：≤0.005
Moisture Content(%):≤0.1
Brand:Thousands Technology
Appearance：light yellow liquid
Viscosity(25 °C): 20-80mPa.s
Acid value:660min mgKOH/g
Free acid:0.5max%
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: AOC
Product family: Gelcoat
Product type: Pre-accelerated spray gelcoat
Grade: Neogel® 8366-W-0100
Application method: Conventional spray or airless spray
Curing system: Standard MEKP, such as Butanox® M-50 or equivalent
Key features: High gloss, high elongation at break, excellent styrene resistance, easy application and repair, excellent spray properties, cures without foaming or microporosity
Product family: Hot Melt Adhesive
Product type: Pressure Sensitive Adhesive (PSA)
Grade: TECHNOMELT® PS 1573 E
Adhesive technology: Hot melt pressure sensitive adhesive
Substrate compatibility: Paper labels, film labels and low surface energy substrates
Key features: Moderate adhesion across various substrates, good initial tack, good low-temperature toughness, suitable for both paper and film labels
Brand: Henkel
Technology:Mold Release
Appearance：Clear, colorlessLMS
Chemical Type：Solvent Based Polymer
Odor：Solven
Cure：Room temperature cure
Cured Thermal Stability：≤400 °C
Application：Mold Sealer
Application Temperature：20 to 60 °C
Specific Benefit：
● No contaminating transfer
● High thermal stability
● Seals mold porosity, scratches or imperfections
Brand:NanYa
Physical State:Solid particles
Epoxy Equivalent Weight (g/eq):200~220
Hydrolyzable chlorine(ppm):500
Brand: Henkel
Technology:Cyanoacrylate
Chemical Type: Ethyl cyanoacrylate
Appearance (uncured):Transparent, colorless to straw colored liquidLMS
Components：One component- requires no mixing
Viscosity：Low
Cure: Humidity