Brand: COVESTRO
NCO content：4.4 ± 0.2 %
Viscosity (23 °C)：7000 ± 1000 mPa·s
Monomeric HDI：< 0.5%
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 120 g/l
Brand: EVONIK
losson drying：<1.5 %
pH-value:3.7 – 4.5
SiO2 content:>99.8 %
specific surfacearea(BET):175 – 225 m²/g
tamped density:Approx. 50 g/l
Brand: AOC
Appearance: transparent thixotropic liquid
Viscosity at 25℃ (#4, rpm2):Typical Value：13500-18500 mPa.s
Viscosity at 25℃ (#4, rpm20):Typical Value：2350-3200 mPa.s
Gel time at 25 ℃: Typical Value：8-12 minute
Brand: BASHAN
Specific Surface Area BET（m²/g）：200±15
pH Value in 4% dispersion:3.8～4.2
Loss on Drying 2h@ 105℃（％）:≤1.5
Loss on Ignition 2h@ 1000℃（％）:≤2.0
Sieve Residue 45μm（％）:≤0.05
Bulk Density （g/l）：40～60
SiO2Content（％）：≥99.8
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand: EVONIK
Molecular weight C10H22N2:170.3g/mol
Equivalent weight:85.2g/val
H-active equipment weight:42.6g/val
Density at 20℃：0.820-0.925gcm3
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):
•Typical Value Base Gelcoat Brush：35000-60000 mPa.s
•Typical Value Base Gelcoat Spray:21000-40000 mPa.s
Viscosity at 25℃ (#4, rpm20):
•Typical Value Base Gelcoat Brush：5700-7300 mPa.s
•Typical Value Base Gelcoat Spray:3500-5200 mPa.s
Gel time at 25 ℃:
•Typical Value Base Gelcoat Brush：12-18 minutes
•Typical Value Base Gelcoat Spray: 8-15minutes
Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67
Brand:Thousands Technology
Appearance: clear cyan purple liquid
Resin casting body color: light color , light blue, vivid color
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time (25 ℃)：≤ 5 min
Density (25 ℃): 0.900-0.922g / min
Resin casting body color: original color
Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color
Brand:Thousands Technology
Appearance: White high viscous paste
Assay:44.0-46.0 %
Grade: DHBP-101-45S-PS
CAS No.: 78-63-7
Form: Paste
Peroxide concentration: 45%
Key function: Crosslinking agent for silicone rubber
Brand:Thousands Technology
Appearance: Yellow viscous liquid
Amine value (mgKOH/g): 600–630
Color (Gardner): ≤ 6
Viscosity (25 °C, mPa·s): 100–300
Brand:Thousands Technology
Appearance: colorless transparent liquid
Epoxy Equivalent Weight(g/eq):0.32
Viscosity(cps/25℃) 5-15mpas
Organic Chlorine（EQ/100g）:≤0.02
Inorganic Chlorine （EQ/100g）：≤0.005
Moisture Content(%):≤0.1
Brand:Thousands Technology
Appearance：light yellow liquid
Viscosity(25 °C): 20-80mPa.s
Acid value:660min mgKOH/g
Free acid:0.5max%
Brand: TR INDUSTRIES
Dry Time: 5-10 minutes@ 72°F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200°F (85 – 93°C)
Color: Off-white
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appreance: Clear-Slight hazy
Viscosity @23℃: 1700-2300 mPa.s
Solids content: 33-35 %
Product type: SMC/BMC resin
Grade: Palapreg® H 856-902
Processing methods: SMC and BMC molding
Product family: Hot Melt Adhesive
Product type: Pressure Sensitive Adhesive (PSA)
Grade: TECHNOMELT® PS 1573 E
Adhesive technology: Hot melt pressure sensitive adhesive
Substrate compatibility: Paper labels, film labels and low surface energy substrates
Key features: Moderate adhesion across various substrates, good initial tack, good low-temperature toughness, suitable for both paper and film labels
Brand: Henkel
Chemical Type: Ethyl cyanoacrylat
Appearance (uncured): Black liquLMS
Components：One part – requires no mix
Viscosity：High
Cure: Humidity
Application: Bonding
Key Substrates：Metals , Plastics and Rubb
Brand: Henkel
Chemical Type: Alkoxyethyl cyanoacrylate
Appearance (uncured):Transparent, colorless to straw colored liquidLMS
Components：One component- requires no mixing
Viscosity：Low
Cure: Humidity
Application: Bonding
Key Substrates：Metals , Plastics and Elastomers