Brand: AOC
Appearance: transparent thixotropic liquid
Viscosity at 25℃ (#4, rpm2):Typical Value：13500-18500 mPa.s
Viscosity at 25℃ (#4, rpm20):Typical Value：2350-3200 mPa.s
Gel time at 25 ℃: Typical Value：8-12 minute
Brand: BASHAN
Specific Surface Area BET（m²/g）：200±15
pH Value in 4% dispersion:3.8～4.2
Loss on Drying 2h@ 105℃（％）:≤1.5
Loss on Ignition 2h@ 1000℃（％）:≤2.0
Sieve Residue 45μm（％）:≤0.05
Bulk Density （g/l）：40～60
SiO2Content（％）：≥99.8
Brand: EVONIK
Molecular weight C10H22N2:170.3g/mol
Equivalent weight:85.2g/val
H-active equipment weight:42.6g/val
Density at 20℃：0.820-0.925gcm3
Brand:Thousands Technology
Appearance: Light yellow transparent liquid
Viscosity（25℃，Pa·s）：0.25-0.45
Gel time（25℃，min）：9-17
Acid value（mgKOH/g）：28-36
Solid content（%）：61-67
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time (25 ℃)：≤ 5 min
Density (25 ℃): 0.900-0.922g / min
Resin casting body color: original color
Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color
Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s