Synolite™ 8175-W-1 is designed for ease of fabrication using hand lay-up, filament winding techniques. Components based on
Synolite™ 8175-W-1 feature excellent fire retardant, low smoke & toxicity properties. And recommended for building & construction , transportation fire retardant applications.
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 45 %
Density: 1.046 g/ml
Brand: INEOS
Dynamic Viscosity: 325 mPa·s (cps)
Kinematic Viscosity: 300 cSt
Styrene Content: 33 %
Density: 1.08 g/ml
Brand:Thousands Technology
Appearance: clear cyan purple liquid
Resin casting body color: light color , light blue, vivid color
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time (25 ℃)：≤ 5 min
Density (25 ℃): 0.900-0.922g / min
Resin casting body color: original color
Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color
Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min