Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value
Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Peel Ply is a fabric layer placed on the surface of a composite laminate which can be removed after curing of the composite to leave a textured surface on the surface of the laminate.
Breathers and bleeders are auxiliary materials used in composite molding to remove air and excess resin, ensuring vacuum integrity and product quality.
Sealant Tape is typically used whenever an air tight seal is required and will adhere to most surfaces. It is most commonly used in the composite manufacturing process of temporary as well as permanent vacuum bagging.
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Brand: AOC
Appearance: pink thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：50000-80000mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：10000-13000mPa.s);（Typical Value Base Gelcoat Spray：7500-9500mPa.s)
Gel time at 25 ℃: (Typical Value Base Gelcoat Brush：12-20min);(Typical Value Base Gelcoat Spray:8-16 min)
Release film ensures that breather fabric or flow mesh does not bond to the curing resin. By use of various perforation patterns, the amount of resin that is bled out of the laminate can be controlled, to achieve the correct fiber ratio within the composite.
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min