This product is the best light color accelerator for unsaturated polyester resin cured at room temperature. Usually it is used with a peroxide-inducing agent such as cyclohexanone peroxide or methyl ethyl ketone, the amount is generally about 0.5% to 2.5% of the resin.It is widely used in FRP, Polyester polywood, polyester household, artificial agate, polyester buttons, casting procss, etc.
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 45 %
Density: 1.046 g/ml
Brand: INEOS
Dynamic Viscosity: 325 mPa·s (cps)
Kinematic Viscosity: 300 cSt
Styrene Content: 33 %
Density: 1.08 g/ml
Brand:Cabot
B.E.T. Surface Area：200 m2/g
pH (4% aqueous slurry)： 3.7 – 4.3
325 Mesh Residue (44 microns)： 0.02% max.
Tamped Density： 50 g/l
Loss on Heating*： < 1.5%
Specific Gravity ：2.2 g/cm3
Wt. per gallon： 18.3 lb
Brand:Thousands Technology
Appearance: clear cyan purple liquid
Resin casting body color: light color , light blue, vivid color
Brand:Thousands Technology
Appearance: clear purple liquid
Resin casting body color: original resin color
Brand: AOC
Appearance: Beige
Viscosity1) @23℃:1200-2000 mPa.s
Gel time, 200g paste cured with 2% M50,23℃:55-65 minutes
Gel_Time2) (25℃ until 35℃):38-41 minutes
Curel_Time2) (25℃-peak)：51-61 minutes
Brand:Thousands Technology
Appearance: clear purple liquid
Gel time(25℃)≤5min
Density(25℃):0.900-0.922g/min
Color of resin casting body: reveal original resin color
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand:Thousands Technology
Appearance: Clear liquid
Color:≤50 Pt-Co
Total active oxygen:10.0-10.3 %
Density:0.99 g/cm³
Viscosity, 20 °C:12 mPa.s