Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-230 mPa.s
Solids content, IR drying：61-63 %
Acid value:16.5-23.5 mgKOH/g
Gel time(25℃to35 °C):22-40 min
Brand: AOC
Appearance: Beige
Viscosity @23℃（20S-1）:670-870 mPa.s
Viscosity @23℃（50S-1）：600-680 mPa.s
Viscosity @23℃（250S-1）：520-580 mPa.s
Solids content, IR drying：74.5-77.5 %
Gel_Time (25 until 35℃):9-11 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance:Clear
Solids content, IR drying:55-63%
Viscosity @23℃:1100-1400 mPa.s
Gel_Time (25 until 35℃):9-15 min
Brand: AOC
Appearance: Clear-sl Hazy
Solids content: 50 – 56 %
Viscosity @23℃，100 s<sup>-1</sup>:450-550 mPa.s
Gel time (25 until 35 ℃): 21-36min
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: AOC
Appreance: Clear-Slight hazy
Viscosity @23℃: 1700-2300 mPa.s
Solids content: 33-35 %
Product type: SMC/BMC resin
Grade: Palapreg® H 856-902
Processing methods: SMC and BMC molding
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Chemical nature: Pre-accelerated unsaturated polyester resin dissolved in styrene
Reactivity: Medium
Viscosity: Low
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: AOC
Product family: Gelcoat
Product type: Pre-accelerated spray gelcoat
Grade: Neogel® 8366-W-0100
Application method: Conventional spray or airless spray
Curing system: Standard MEKP, such as Butanox® M-50 or equivalent
Key features: High gloss, high elongation at break, excellent styrene resistance, easy application and repair, excellent spray properties, cures without foaming or microporosity
Product family: Hot Melt Adhesive
Product type: Pressure Sensitive Adhesive (PSA)
Grade: TECHNOMELT® PS 1573 E
Adhesive technology: Hot melt pressure sensitive adhesive
Substrate compatibility: Paper labels, film labels and low surface energy substrates
Key features: Moderate adhesion across various substrates, good initial tack, good low-temperature toughness, suitable for both paper and film labels
Brand: Henkel
Chemical Type: Ethyl cyanoacrylat
Appearance (uncured): Black liquLMS
Components：One part – requires no mix
Viscosity：High
Cure: Humidity
Application: Bonding
Key Substrates：Metals , Plastics and Rubb
Brand: Henkel
Chemical Type: Epoxy
Appearance (Resin):Off-whiteLMS
Appearance (Hardener):greenLMS
Appearance (Mixture):Off-whiteLMS
Components:Two part – Resin & Hardener
Mix Ratio, by weight -Resin : Hardener:100:4
Mix Ratio, (by volume)Resin : Hardener:2.5:1
Cure:Room temperature cure after mixing
Brand: Henkel
Chemical Type: Epoxy
Appearance (Mixed):Steel Colored Paste
Mix Ratio, by volume -Resin : Hardener|：1:1
Mix Ratio, by weight -Resin : Hardener：100 : 56.5
Cure:Room temperature cure after mixing
Application：North America – Metal Repair
Specific Benefit：
● Hardens in ten minutes
● Non sagging
● Steel filled system – cures to metal-like finish
● Bonds to steel, cast iron,stainless steel, concrete,copper, aluminum, and clean and abraded bronze
Brand: Henkel
Technology:Silicone
Chemical Type:Oxime silicone
Appearance:Black pasteLMS
Components:One component -requires no mixing
Viscosity:Thixotropic paste
Cure：Room temperature vulcanizing (RTV)
Application:Sealing
Specific Benefits:Excellent resistance to automotive engine oils.
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:White or light creme suspensionLMS
Odor:Hydrocarbon
Cure：Room temperature cure
Cured Thermal Stability:≤280 °C
Application:Release Coatings
Application Temperature:15 to 35 °C
Specific Benefit:
● High gloss finish
● Multiple releases
● Minimal mold build-up
● Easy application
● Low odor
● Visible mold coverage
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:13 to 135 °C
Brand: Henkel
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:20 to 60 °C
Specific Benefit:
● Fast drying
● Non-contaminating transfer
● High thermal stability
● Non-CFC
● No mold build-up
Brand: Henkel
Technology:Mold Release
Chemical Type: Solvent Based Polymer
Appearance:Clear, colorlessLMS
Odor:Solvent
Cure：Room temperature cure
Cured Thermal Stability:≤400 °C
Application:Release Coatings
Application Temperature:20 to 60 °C
Specific Benefit:
● Fast drying
● Non-contaminating transfer
● High thermal stability
● Non-CFC
● No mold build-up
Brand: Henkel
Chemical Type: Epoxy
Appearance (Resin):White liquidLMS
Appearance (Hardener)：Gray liquidLMS
Components：Two component – requires mixing
Mix Ratio, by volume -Resin : Hardener：2 : 1
Mix Ratio, by weight -Resin : Hardener：100:50
Cure:Room temperature cure
Application：Bonding