Palatal® P 65-972 is special for varied kinds of FRP moulding products that have a high resistance to heat deformation. Pultrusion, filament winding, RTM, and high-filler moulding and
poly-concrete are all recommended.
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min