ZC-907 is a high-performance phenolic vinyl ester resin with a relatively light product color. In addition to its excellent high-temperature corrosion resistance and oxidation resistance, it also possesses superior solvent resistance, effectively exhibiting its properties at temperatures up to 180°C.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Casting, Compression Molding, Continuous Molding, Filament Winding, Hand Lay-up, Pultrusion |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
| Appearance: | light yellow transparent liquid |
| Density: | 1.06±0.02kg/L |
| Viscosity: | 430±150 cps (LVT#3-60rpm/25℃) |
| Solid content: | 62±1.5% (55%MEKPO: 1.2%, 6% cobalt octanoate 0.4%, 100%DMA: 0.05%, temperature: 25℃ water bath) |
| Shelf life: | 4 months (below 25℃) |
| Tensile strength: | 76-90MPa (ASTM D 638) |
| Tensile modulus: | 3.4-3.7GPa (ASTM D 638) |
| Elongation: | 2.5-4.0% (ASTM D 638) |
| Flexural strength: | 124-145MPa (ASTM D 790) |
| Flexural modulus: | 3.7-4.1GPa (ASTM D 790) |
| Heat deformation temperature: | 144-150℃ (ASTM D 648) |
| Hardness: | 40-46 Barcol (ASTM D 2583) |
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Appearance:pink liquid
Acid Value：17-24mgKOH/g
Viscosity，25℃：0.3-0.4 Pa.s
Solid Content：58-64%
Gel time：25-43min
Appearance:Light yellow transparent viscous liquid
Acid Value:14-20mgKOH/g
Viscosity，25℃:0.14-0.16Pa.s
Solid Content:52-58%
Gel time:25-38min
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Appearance:Clear liquid,no visible mechanical impurity
Colour(Hazen):40 Max
Epoxy Equivalent(g/mol):210-230
Hydrolytic Chlorine (%):0.50 Max
Inorg.Cl （mg/kg）:50 Max
Volatile /150℃,40min(%):0.6 Max
Softening Point(℃):14-23
Appearance: Semi-solid
Epoxy equivalent (g/eq): 170-190
*Hue(G): 3.0Max.
Flash point (℃): 250↑
Solution viscosity (25℃): H~K
Density (g/cm³ 20℃): 1.18