A high production paste wax mold release with excellent breakdown characteristics for fast, even coverage. A firm carnauba based mold release paste wax blended with other synthetic waxes for use in various thermo-set composite molding applications.
| Supplier | |
|---|---|
| Additive Classification | Mold Release Wax |
| Industry | Automotive & Transportation, Building & Construction, Electrical & Electronics, Wind Energy |
As a release agent for composite molding on all FRP tooling, metal and other hard surface molds.
On new or reconditioned tooling, suggest use of our sealer glaze TR-301 or TR-910 semi-permanent sealer prior to waxing for added release, gloss and mold life. Apply wax with sponge applicator in thin even circular motion to the mold surface. Allow to haze dry (approx. 5-10 min) depending on ambient temperature and polish wipe to gloss finish with soft cloth (do not use microfiber cloth). For new or reconditioned molds, apply a minimum of 6 coats of paste wax, waiting approximately 30-60 minutes between applications for the wax to set & harden after the polish wipe. Best results are obtained, if after application, mold is allowed to stand overnight and a subsequent final coat of wax release applied the following day prior to gel coating. Follow with a coat of wax for the first 2-3 parts released. Then determine how many parts can be effectively produced before re-waxing is required. This will vary depending on molding condition, configuration, resin, mold cycles, effective cure of production gel coat and other factors.
Brand:Polylite
Appearance:Hazy
Acid Value:8-15mgKOH/g
Viscosity，25℃:1.8-2.2Pa.s
Solid Content:54-59%
Gelation time,25℃:20-38min
Brand:Perkadox®
Chemical family:Organic peroxide
CAS number:80-43-3
Physical form:Crystal
Molecular Weight:270.4
Concentration:5.86% min.
Chemical name:Dicumyl peroxide
Brand:Trigonox®
Chemical family:Organic peroxide
CAS number:6731-36-8
Physical form:Liquid
Molecular Weight:302.5
Chemical name:1,1-Di(tert-butylperoxy)-3,3,5-trimethylcyclohexane, 90% solution in isododecane
Brand:Polylite
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Brand:Polylite
Appearance: Clear liquid,no visible mechanical impurity
Epoxy Equivalent (g/eq): 176–184
Color (Gardner): Max 1.0
Flash Point (℃): Above 150
Viscosity (cps, at 25℃): 8000–11000
Hydrolyzable Chlorine Content (ppm): Below 1000
Specific Gravity (g/cm³, 25℃): 1.16
True high-gloss paste wax.
Withstands high-temperature exothermic reactions of resins and does multiple releases easily.
Contains carnauba wax, synthetic waxes and high-temperature resistant resins for effective multiple releases of plastic parts through numerous cycles.