Brand:SINOCHEM HOLDINGS
Appearance：Clear liquid, no visible mechanical impurity
Colour (Hazen)：40 Max
Epoxy Equivalent (g/mol)：184～195
Hydrolytic Chlorine (%)：0.20 Max
Inorganic Chlorine (mg/kg)：50 Max
Volatile /150℃,40min (%)：0.50 Max
Viscosity/25 (mPa.s) ℃：10000-16000
Brand:Dow
Epoxide Equivalent Weight (g/eq)：182 – 192
Epoxide Percentage (%)：22.4 – 23.6
Epoxide Group Content (mmol/kg)：5200 – 5500
Color (Platinum Cobalt)：75 Max.
Viscosity @ 25°C (mPa•s)：11000 – 14000
Hydrolyzable Chloride Content (ppm)：500 Max.
Shelf Life (Months)：24
Brand: RESONAC
Tensile Strength: 69~89 MPa
Tensile Elongation at break: 4.0~5.0 %
Flexural Strength: 130~140 MPa
Flexural Modulus: 2.7~3.1 GPa
Heat Distortion Temperature:100~110 ℃
Barcol Hardness:40
Volume Shrinkage:7.5~8.5%
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1200 mPas at ISO 2555
Viscosity, cone&plate:320 mPas at ISO 2884
Styrene content: 44% at ISO 4864
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1,5% MEKP-50:35 min at D006
Peak exotherm, 1% MEKP-50:170 °C at D006
Brand: INEOS
Property at 23 °C
Viscosity, Brookfield RV2, 10 rpm:1400 mPas at ISO 2555
Viscosity, cone&plate:180 mPas at ISO 2884
Styrene content: 41% at ASTM D 1644
Density:1.1 kg/dm3 at ISO 2811
Geltime, 1% MEKP-50:40 min at Hc-04a
Peak exotherm:110 °C at Hc-04a
Brand: INEOS
Viscosity at 25°C:
Brookfield RVT sp3, 60rpm:385 mPas at ISO 2555
Brookfield RVT sp3, 6rpm:900 mPas at ISO 2555
Styrene Content:40% at SFS 4864
Index of thixotropy:2.33
Brand: INEOS
Dynamic Viscosity: 370 mPa·s (cps)
Kinematic Viscosity: 350 cSt
Styrene Content: 45 %
Density: 1.046 g/ml
Brand: AOC
Geltime at 25℃ (2ml Butanox M50):10-16 minutes
Peak temperature: 175-190 ℃
Viscosity at 25℃ (#4, rpm2): 30000-36000 mPa.s
Viscosity at 25℃ (#4, rpm20): 4000-5500 mPa.s
Brand: AOC
Appearance: Hazy
Viscosity, 23℃: 620-680 mPa.s
Viscosity, 23℃: 590-630 mPa.s
Viscosity, 23℃: 530-560 mPa.s
Solids content, IR: 68-71 % TM 2033
Gel time 25 to 35℃: 38-42 min