Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min
Brand: AOC
Appreance: Clear-Slight hazy
Viscosity @23℃: 1700-2300 mPa.s
Solids content: 33-35 %
Brand: AOC
Appearance:Clear
Solids content, IR drying:64-68%
Viscosity @23℃:300-500 mPa.s
Gel_Time (25 until 35℃):30-45 min
Brand: AOC
Appearance: Clear
Solids content, IR drying:53-58%
Acid value:4-8 mgKOH/g
Viscosity @23℃:180-250 mPa.s
Brand: AOC
Brand: Henkel
Chemical Type: Epoxy
Appearance :Light yellow solid
Brand: Henkel
Chemical Type: Ethyl cyanoacrylat
Appearance (uncured): Black liquLMS
Components：One part – requires no mix
Viscosity：High
Cure: Humidity
Application: Bonding
Key Substrates：Metals , Plastics and Rubb
Brand: Henkel
Chemical Type: Epoxy
Appearance (Resin):Off-whiteLMS
Appearance (Hardener):greenLMS
Appearance (Mixture):Off-whiteLMS
Components:Two part – Resin & Hardener
Mix Ratio, by weight -Resin : Hardener:100:4
Mix Ratio, (by volume)Resin : Hardener:2.5:1
Cure:Room temperature cure after mixing
Secondary Cure:Heat
Application:Bonding
Specific Benefit：
● Machineable
● Sandable
● High service temperature
● Low outgassing properties
● Excellent environmental resistance
Brand: Henkel
Chemical Type: Epoxy
Appearance (Mixed):Steel Colored Paste
Mix Ratio, by volume -Resin : Hardener|：1:1
Mix Ratio, by weight -Resin : Hardener：100 : 56.5
Cure:Room temperature cure after mixing
Application：North America – Metal Repair
Specific Benefit：
● Hardens in ten minutes
● Non sagging
● Steel filled system – cures to metal-like finish
● Bonds to steel, cast iron,stainless steel, concrete,copper, aluminum, and clean and abraded bronze
Brand: Henkel
Technology:Mold Release
Appearance：Clear, colorlessLMS
Chemical Type：Solvent Based Polymer
Odor：Solven
Cure：Room temperature cure
Cured Thermal Stability：≤400 °C
Application：Mold Sealer
Application Temperature：20 to 60 °C
Specific Benefit：
● No contaminating transfer
● High thermal stability
● Seals mold porosity, scratches or imperfections