Neogel® 8300-W-9617 is a high performance gelcoat, which was developed for manufacturing GRP moulds.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Filament Winding, Hand Lay-up, Spraying |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
Neogel® 8300-W-9617 is a high gloss gelcoat, easy to repair. It has good resilience and excellent resistance to styrene.
Neogel® 8300-W-9617 is pre-accelerated thixotropic, ready for use and available in a wide range of colours, in the
following types:
• Spray type (Neogel® 8300-W-9617 S)
• Brush type (Neogel® 8300-W-9617)
In order to obtain optimum performance it is advisable to operate as follows:
• Temperature between 18℃ and 25℃
• Cure with recommended MEKP* 50% solution, adjust
amount between 1.0-2.0%
• Thickness of the film 700-900g/m²
*Butanox M50 (Akzo Nobel)
True high-gloss paste wax.
Withstands high-temperature exothermic reactions of resins and does multiple releases easily.
Contains carnauba wax, synthetic waxes and high-temperature resistant resins for effective multiple releases of plastic parts through numerous cycles.
Brand:Trigonox®
Chemical family:Organic peroxide
CAS number:75-91-2
Physical form:Liquid
Molecular Weight:90.1
Chemical name:tert-Butyl hydroperoxide, 70% solution in water
Brand：Perkadox®
CAS number：94-36-0
Molecular Weight：242.2
Concentration：3.20-3.37%
Chemical name：Dibenzoyl peroxide, paste, 50% in dipropylene glycol dibenzoate and water
Brand:Butanox®
Chemical family:Organic peroxide
CAS number:1338-23-4
Physical form:Liquid
Chemical name:Methyl ethyl ketone peroxide
Brand:Polylite
Appearance:Clear liquid,no visible mechanical impurity
Colour(Hazen):40 Max
Epoxy Equivalent(g/mol):210-230
Hydrolytic Chlorine (%):0.50 Max
Inorg.Cl （mg/kg）:50 Max
Volatile /150℃,40min(%):0.6 Max
Softening Point(℃):14-23
Brand:Polylite
Appearance: light yellow transparent liquid
Density: 1.06±0.02kg/L
Viscosity: 430±150 cps (LVT#3-60rpm/25℃)
Solid content: 62±1.5%
Gelation time: 15-25 minutes