Atlac® 490-901 resin based laminates feature excellent retention of mechanical properties at elevated temperature. Furthermore a good chemical resistance to acids, aqueous solution of salt and organic solvents.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Continuous Molding, Filament Winding, Hand Lay-up, Pultrusion, Spraying |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
Atlac® 490-901 is designed for the following process such as hand lay-up, spray-up, filament winding and pultrusion,etc.
The solvent resistance of Atlac® 490-901 resin makes it excellent for GRP tanks, pipes and linings for handling liquid hydrocarbons. Atlac® 490-901 resin is approved as matrix materials for FRP tanks for underground fuel storage according to BRL K548/01. The resin can also be used to formulate flake glass lining compounds and is
recommended for the GRP reinforcement layers of equipment with liners of polypropylene.The resin shows excellent retention of laminate properties at elevated
temperature. Furthermore a good chemical resistance to acids, aqueous solution of salt and organic solvents.
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: AOC
Solids content: 49.5 – 52.5 %
Gel time (25 until 35 ℃): 25.5 – 31.5min
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 64-68 %
Viscosity @23℃: 400-550 mPa.s
Gel_Time (25 until 35 °C): 12-25 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min