Characteristics
- No chlorine solvent
- Smooth surface, easy to separate
- Wide application—applied to most polyester materials
- Dried and solidified under room temperature
- No transfer
- No residual
Material Physical and Chemical Properties
Appearance: Clear liquid
Odor: Hydrocarbon
Solvent: Polysiloxane/Fluororesin/hydrocarbon
Relative Density: 0.732 (+/-0.02)
Flash Point: 26℃
Shelf Life: 1 year
Cured Thermal Stability: ≤ 330℃（≤626°F）
Application Temperature: 13 to 135℃（55 to 275°F）
Notice: Sensitive to humidity, be safely sealed when not being used. Keep it in a well ventilate condition when being used.
Application of release agent (refer to the product safety data before use) :
1. Brush or wipe Deawa® 5380 with a a clean dust-free cloth on mold surfaces at room temperature less than 60° C in a well ventilated area.( can’t use non-woven, because Deawa® 5380 solvents dissolve the adhesive of non-woven.) It will be better to brush or wipe from the side of the mold to the other side orderly.
2. Use a new clean dry cloth, from outside to inside circularly wipe the surface before the wet sealer evaporate, until the mold surface is dry and clear.Then the first layer of release agent film is coated on mold surface, it should be a layer of smooth, continuous film.(pls use a clear and dry cotton cloth to wipe the mold surface again after coated the release agents)
3. After solvent evaporated, repeat step1 and step2 to apply the 2nd layer up. Generally requie 2 ~5times coating, 10~15 minitues interval of each coating, the film should be dry and not sticky.
4. Allow the final coat to cure for 20 to 30 minutes at room temperature. Note the lower temperature will cause more cure time. Avoid use the mold after just wipe release agent, the release agent film should be solidified completely to be used in subsequent process.
5. When any release difficulty is detected, can choose to re-coat the whole mold again, or only the area with problems.If the mold temperature is higher than 135 ° C, make sure Deawa® DW-5380 is dry thoroughly before reused.