ZC-907 is a high-performance phenolic vinyl ester resin with a relatively light product color. In addition to its excellent high-temperature corrosion resistance and oxidation resistance, it also possesses superior solvent resistance, effectively exhibiting its properties at temperatures up to 180°C.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Casting, Compression Molding, Continuous Molding, Filament Winding, Hand Lay-up, Pultrusion |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
| Appearance: | light yellow transparent liquid |
| Density: | 1.06±0.02kg/L |
| Viscosity: | 430±150 cps (LVT#3-60rpm/25℃) |
| Solid content: | 62±1.5% (55%MEKPO: 1.2%, 6% cobalt octanoate 0.4%, 100%DMA: 0.05%, temperature: 25℃ water bath) |
| Shelf life: | 4 months (below 25℃) |
| Tensile strength: | 76-90MPa (ASTM D 638) |
| Tensile modulus: | 3.4-3.7GPa (ASTM D 638) |
| Elongation: | 2.5-4.0% (ASTM D 638) |
| Flexural strength: | 124-145MPa (ASTM D 790) |
| Flexural modulus: | 3.7-4.1GPa (ASTM D 790) |
| Heat deformation temperature: | 144-150℃ (ASTM D 648) |
| Hardness: | 40-46 Barcol (ASTM D 2583) |