ZC-5717resin is an unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard diols as the main raw materials. It has been dissolved in styrene crosslinked monomer and has high viscosity and high reactivity.
Supplier | |
---|---|
Resin Type | Unsaturated Polyester Resin |
Pre-promotion Thixotropy | / |
Molding Process | Compression Molding |
Industry | Building & Construction |
ZC-5717 resin light color, good stability, strength and toughness. Suitable for making BMC manhole cover, traffic guardrail base and other special products.
Item | Range | Unit | Test Standard | |
Appearance | Light yellow transparent viscous liquid | — | — | |
Acid Value | 14-22 | mg KOH/g | GB/T 2895-2008 | |
Viscosity, 25℃ | 1.6-2.3 | Pa.s | GB/T 7193-2008 | |
Solid Content | 70-76 | % | GB/T 7193-2008 | |
Gel Time, 25℃ | 8.5-10.5 | min | GB/T 7193-2008 | |
Thermal Stability, 80℃ | ≥24 | h | GB/T 7193-2008 | |
Responsiveness | Gel Time | 40-120 | s | GB/T 24148.6-2009 |
Curing Time | 100-180 | s | ||
Exothermic Peak | 225-265 | ℃ |
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity,25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Appearance:pink liquid
Acid Value:17-24mgKOH/g
Viscosity,25℃:0.3-0.4 Pa.s
Solid Content:58-64%
Gel time:25-43min
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Physical State:liquid
Epoxy Equivalent (g/eq):184~190
Color (Gardner):1.0max
Flash Point (℃):150↑
Viscosity (cps, at 25℃):12000~15000
Hydrolyzable Chlorine Content (ppm):1000↓
Specific Gravity (g/cm³, 25℃):1.16
Appearance: Clear liquid,no visible mechanical impurity
Epoxy Equivalent (g/eq): 176–184
Color (Gardner): Max 1.0
Flash Point (℃): Above 150
Viscosity (cps, at 25℃): 8000–11000
Hydrolyzable Chlorine Content (ppm): Below 1000
Specific Gravity (g/cm³, 25℃): 1.16
Appearance: light yellow transparent liquid
Density: 1.06±0.02kg/L
Viscosity: 430±150 cps (LVT#3-60rpm/25℃)
Solid content: 62±1.5%
Gelation time: 15-25 minutes