ZC-5211 resin is a phthalic unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard diols as the main raw materials. It has been dissolved in crosslinked monomers such as styrene and has medium viscosity and low reactivity.
| Supplier | |
|---|---|
| Resin Type | Unsaturated Polyester Resin |
| Pre-promotion Thixotropy | TP |
| Molding Process | Casting |
| Industry | Home Renovation |
ZC-5211 resin light color, high transparency, shrinkage, stable curing, good operability, suitable for ordinary transparent crafts.
| Property | Value | Unit | TM |
| Appearance | Yellowish transparent viscous liquid | – | – |
| Acid Value | 14-20 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.35-0.45 | Pa.s | GB/T 7193-2008 |
| Solid Content | 61-67 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel Time | 4-6 | min | GB/T 7193-2008 |
Brand:Perkadox®
Chemical family:Organic peroxide
CAS number:80-43-3
Physical form:Crystal
Molecular Weight:270.4
Concentration:5.86% min.
Chemical name:Dicumyl peroxide
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:14-22 mg KOH/g
Viscosity, 25℃:1.6-2.3 Pa.s
Solid Content:70-76 %
Gel Time, 25℃:8.5-10.5 min
Thermal Stability, 80℃:≥24h
Brand:Polylite
Physical State:liquid
Epoxy Equivalent (g/eq):184～190
Color (Gardner):1.0max
Flash Point (℃):150↑
Viscosity (cps, at 25℃)：12000～15000
Hydrolyzable Chlorine Content (ppm)：1000↓
Specific Gravity (g/cm³, 25℃)：1.16
Brand:Polylite
Appearance: Clear liquid,no visible mechanical impurity
Epoxy Equivalent (g/eq): 176–184
Color (Gardner): Max 1.0
Flash Point (℃): Above 150
Viscosity (cps, at 25℃): 8000–11000
Hydrolyzable Chlorine Content (ppm): Below 1000
Specific Gravity (g/cm³, 25℃): 1.16
Brand:Perkadox®
Chemical family:Organic peroxide
CAS number:94-36-0
Physical form:Granular powder
Chemical name:Dibenzoyl peroxide
Brand:Butanox®
Chemical family:Organic peroxide
CAS number:1338-23-4
Physical form:Liquid
Chemical name:Methyl ethyl ketone peroxide, solution in dimethyl phthalate