Epoxy Resin ZC-44 is a liquid resin manufactured from bisphenol-A and epichlorohydin. It is recognized as a standard from which many variations have been developed .A wide variety of curing agents is available to cure liquid epoxy resins at ambient conditions. The most frequently used are aliphatic polyamines, polyamides, amidoamines, cycloaliphatic amines and modified versions of these curing agents. These systems are sometimes cured at an elevated temperature to improve selected properties such as chemical resistance and glass transition temperature. Elevated temperature cures are necessary and long post-cures are required to develop full end properties if anhydride of catalytic curing agents are employed.
| Supplier | |
|---|---|
| Resin Type | Epoxy Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Filament Winding, Hand Lay-up, Pultrusion |
| Industry | Automotive & Transportation, Electrical & Electronics, Marine Vessels, Paints & Coatings |
This product is suitable for use in applications such as:-Adhesives -Filament winding -Casting and Tooling -Civil Engineering -Composites -Automotive Coatings -Can Coating -Coil Coating -Marine & Protective Coatings.
| Property | Value | Unit | TM |
| Appearance | Transparent liquid,free of mechanicalimpurities | – | – |
| Epoxy equivalent | 450-500 | g/mol | GB/T 2895-2008 |
| Hydrolyzed chlorine | 0.20max | % | GB/T 7193-2008 |
| Inorganic chlorine | 50max | mg/kg | GB/T 7193-2008 |
| Volatile matter | 0.50max | mg/kg | GB/T 7193-2008 |
| Viscosity /25℃ | 8000-15000 | mPa•s | GB/T 7193-2008 |
Brand:Trigonox®
Chemical family:Organic peroxide
CAS number:6731-36-8
Physical form:Liquid
Molecular Weight:302.5
Chemical name:1,1-Di(tert-butylperoxy)-3,3,5-trimethylcyclohexane, 90% solution in isododecane
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:19-25mgKOH/g
Viscosity，25℃:0.30-0.60Pa.s
Solid Content:59-66%
Thermal Stability,80℃:≥24h
Gel time:12-30min
Brand:Polylite
Appearance:Light yellow transparent viscous liquid
Acid Value:14-22 mg KOH/g
Viscosity, 25℃:1.6-2.3 Pa.s
Solid Content:70-76 %
Gel Time, 25℃:8.5-10.5 min
Thermal Stability, 80℃:≥24h
Brand:Polylite
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Brand:Polylite
Appearance: Brown-yellow transparent liquid
Density: 1.05-1.07kg/L
Viscosity: 1 350±100cps
Solid content: 55±1%
Gelation time: 2 15±5min
Shelf life: 6 months (below 25℃)
Brand:Polylite
Appearance: light yellow transparent liquid
Density: 1.06±0.02kg/L
Viscosity: 430±150 cps (LVT#3-60rpm/25℃)
Solid content: 62±1.5%
Gelation time: 15-25 minutes