exterior condition：quiet
Solids content, infrared drying：58-67 %
Viscosity @23℃：300-500 mPa.s
Gel time (25°C to 35°C)：5-15 minutes
Gel time at 25°C:10-16 minutes
exothermic peak:175-190 ℃
Viscosity at 25°C (rpm2):30000-36000 mPa.s
Viscosity at 25°C (rpm20):4000-5500 mPa.s
exterior condition:muddy
Viscosity 23°C Z2, 2s-1:620-680 mPa.s
Viscosity 23°C Z2, 50s-1:590-630mPa.s
Viscosity 23°C Z2, 250s-1:530-560mPa.s
Solid content:68-71%
Gel time 25-35℃:38-42minutes
Curing time 25℃-exothermic peak:46-56minutes
exothermic peak:110-120 ℃
Gel time at 25°C:10-16 minutes
exothermic peak:175-190 ℃
Viscosity at 25°C (rpm2):30000-36000 mPa.s
Viscosity at 25°C (rpm20):4000-5500 mPa.s
Appearance:Hazy
Acid Value:8-15mgKOH/g
Viscosity，25℃:1.8-2.2Pa.s
Solid Content:54-59%
Gelation time,25℃:20-38min
Physical State: Liquid
Epoxy Equivalent (g/eq): 176–184
Color (Gardner): Max 1.0
Flash Point (℃): Above 150
Viscosity (cps, at 25℃): 8000–11000
Hydrolyzable Chlorine Content (ppm): Below 1000
Specific Gravity (g/cm³, 25℃): 1.16
Physical State:liquid
Epoxy Equivalent (g/eq):184～190
Color (Gardner):1.0max
Flash Point (℃):150↑
Viscosity (cps, at 25℃)：12000～15000
Hydrolyzable Chlorine Content (ppm)：1000↓
Specific Gravity (g/cm³, 25℃)：1.16
Appearance:Light yellow transparent viscous liquid
Acid Value:19-25mgKOH/g
Viscosity，25℃:0.30-0.60Pa.s
Solid Content:59-66%
Thermal Stability,80℃:≥24h
Gel time:12-30min
Appearance:pink liquid
Acid Value：17-24mgKOH/g
Viscosity，25℃：0.3-0.4 Pa.s
Solid Content：58-64%
Thermal Stability,80℃：≥24h
Gel time：25-43min
Appearance:Light yellow ransparent viscous liquid
Acid Value:19-25mgKOH/g
Viscosity，25℃:0.30-0.60Pa.s
Solid Content:59-65%
Thermal Stability,80℃:≥24h
Gelation time,25℃:6-18
Appearance:Light yellow transparent viscous liquid
Acid Value:20-26mgKOH/g
Viscosity，25℃:0.7-0.8Pa.s
Solid Content:62-68%
Thermal Stability,80℃:≥24
Gel time:6-18
Appearance:Light yellow transparent viscous liquid
Acid Value:14-20mgKOH/g
Viscosity，25℃:0.14-0.16Pa.s
Solid Content:52-58%
Gel time:25-38min
Appearance:Clear liquid,no visible mechanical impurity
Colour(Hazen):40 Max
Epoxy Equivalent(g/mol):210-230
Hydrolytic Chlorine (%):0.50 Max
Inorg.Cl （mg/kg）:50 Max
Volatile /150℃,40min(%):0.6 Max
Softening Point(℃):14-23
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Appearance:Light yellow transparent viscous liquid
Acid Value:14-22 mg KOH/g
Viscosity, 25℃:1.6-2.3 Pa.s
Solid Content:70-76 %
Gel Time, 25℃:8.5-10.5 min
Thermal Stability, 80℃:≥24h
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %