Brand: AOC
Geltime at 25℃ (2ml Butanox M50):10-16 minutes
Peak temperature: 175-190 ℃
Viscosity at 25℃ (#4, rpm2): 30000-36000 mPa.s
Viscosity at 25℃ (#4, rpm20): 4000-5500 mPa.s
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):35000-60000 mPa.s
Viscosity at 25℃ (#4, rpm20):5700-7300 mPa.s
Geltime at 25℃: 12-18 min
Brand: AOC
Appearance: Hazy
Viscosity, 23℃: 620-680 mPa.s
Viscosity, 23℃: 590-630 mPa.s
Viscosity, 23℃: 530-560 mPa.s
Solids content, IR: 68-71 % TM 2033
Gel time 25 to 35℃: 38-42 min
Brand:NanYa
Physical State:Solid
Epoxy Equivalent Weight g/eq :380～410
Soften point ℃: 64～74
Hydrolyzable chlorine PPM :200 max
Br content % :46～50
Color Gardner: 1 max
Brand:NanYa
Epoxy Equivalent Weight (g/eq): 184～190
Color (Gardner) :1.0max
Flash Point (℃) :150↑
Viscosity(cps，at 25 ℃) :12000～15000
Hydrolyzabie chlorine (ppm) :1000↓
Density (g/cm3 25℃) :1.16
Brand: AOC
Appearance: Clear
Viscosity @23℃:1600-1900 mPa.s
Solids content：64-67 %
Acid value:14-19 mgKOH/g
Gel time(80-140oC):40-70 s
Brand: AOC
Appreance: Clear
Viscosity @23℃: 1300-1600 mPa.s
Solids content: 59-63 %
Gel time 80-140°C: 70-110 s
Brand: AOC
Appearance: clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:55-61%
Acid value:8-14 mgKOH/g
Gel time(25℃to35 °C):15-25 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-250 mPa.s
Solids content, IR drying:52-58 %
Acid value:11-18 mg KOH/g
Gel time(25℃to35 °C):40-70 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:54-59 %
Acid value:8-15 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Brand: AOC
Appearance: Clear
Viscosity @23℃:400-550 mPa.s
Solids content, IR drying:59-65 %
Acid value:20-26 mgKOH/g
Gel_time1(25℃ until 35 °C):15-22 min
Gel_time2 (66℃ until 88 °C):4.5-6.6 min
Cure time2(66℃ until peak):6.5-8.6 min
Brand: AOC
Appearance: Hazy
Viscosity @23℃:180-220 mPa.s
Solids content, IR drying:56-62%
Acid value:10-18 mgKOH/g
Gel time(25℃to35 °C):20-38 min
Peel Ply is a fabric layer placed on the surface of a composite laminate which can be removed after curing of the composite to leave a textured surface on the surface of the laminate.
Brand：Perkadox®
Chemical family：Organic peroxide
CAS number：2212-81-9, 25155-25-3
Physical form：Powder
Molecular Weight：338.5
Concentration：3.7-3.9%
Chemical name：Di(tert-butylperoxyisopropyl) benzene
Brand:Perkadox®
Chemical family:Organic peroxide
CAS number:25155-25-3, 2212-81-9
Physical form:Flakes
Molecular Weight:338.5
Concentration:9.26% min.
Chemical name:Di(tert-butylperoxyisopropyl)benzene
Brand：Perkadox®
Chemical family：Organic peroxide
CAS number：15520-11-3
Physical form：Powder
Molecular Weight：398.5
Chemical name：Di(4-tert-butylcyclohexyl) peroxydicarbonate