Neogel® 8300-W-9617S is a high performance gelcoat, which was developed for manufacturing GRP moulds.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Filament Winding, Hand Lay-up, Spraying |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
Neogel® 8300-W-9617S is a high gloss gelcoat, easy to repair. It has good resilience and excellent resistance to styrene.
Neogel® 8300-W-9617S is pre-accelerated thixotropic, ready for use and available in a wide range of colours, in the following types:
• Spray type (Neogel® 8300-W-XXXX S)
• Brush type (Neogel® 8300-W-XXXX)
In order to obtain optimum performance it is advisable to operate as follows:
• Temperature between 18℃ and 25℃
• Cure with recommended MEKP* 50% solution, adjust amount between 1.0-2.0%
• Thickness of the film 700-900g/m²
*Butanox M50 (Akzo Nobel)
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: AOC
Appearance: Thixotropic liquid
Viscosity at 25℃ (#4, rpm2):(Typical ValueBase Gelcoat Brush：26000-45000 mPa.s);（Typical Value Base Gelcoat Spray：22000-40000 mPa.s)
Viscosity at 25℃ (#4, rpm20)：(Typical ValueBase Gelcoat Brush：6500-10000 mPa.s);（Typical Value Base Gelcoat Spray：3500-5000 mPa.s)
Gel time at 25 ℃: 10-20 min