Components based on Atlac® 590UHT feature superior retention of mechanical properties at high temperature, and superior corrosion to oxidizing chemicals and solvents etc.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Filament Winding, Hand Lay-up, Spraying |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
Atlac® 590UHT resin is the preferred choice for applications with high operating/design temperatures. This resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding,compression molding and resin transfer molding techniques.
Atlac® 590UHT resin has been applied in chemical storage tanks,pipes, flue gas desulfurization systems (FGD), stacks, scrubbers,ducts.
Atlac® 590UHT resin has excellent resistance to organic solvents due to itself high crosslinking density
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: AOC
Solids content: 49.5 – 52.5 %
Gel time (25 until 35 ℃): 25.5 – 31.5min
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 64-68 %
Viscosity @23℃: 400-550 mPa.s
Gel_Time (25 until 35 °C): 12-25 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min