Atlac® 590Z provides excellent thermal and chemical resistance against solvents, acids and oxidizing media like chlorine. The resin offers high retention of strength at elevated temperatures.
| Supplier | |
|---|---|
| Resin Type | Vinyl Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Filament Winding, Hand Lay-up, Spraying |
| Industry | Automotive & Transportation, Building & Construction, Home Renovation, Marine Vessels, Petrochemical, Wind Energy |
Atlac® 590Z is a styrene solution of phenolic modified vinyl resin with moderate reactivity and viscosity. Atlac® 590Z offers excellent high temperature stability and corrosion resistance to organic solvents, acids and oxidizing media such as chlorine, as well as high temperature strength retention. Atlac® 590Z is suitable for most production processes, especially for filament winding, centrifugal casting, hand lay-up and spray-up. It can also be used to prepare glass flake coating and cement paste.
To make chemical sourcing more efficient reliable, and intelligent
Every process of our packaging is very strict
just to betterdeliver the goods to your hands!
Brand: AOC
Appearance: Clear
Solids content: 67 – 71 %
Viscosity @23℃:450-550 mPa.s
Gel time (25 until 35 ℃): 28-38min
Brand: AOC
Solids content: 49.5 – 52.5 %
Gel time (25 until 35 ℃): 25.5 – 31.5min
Brand: AOC
Appearance: Yellow and hazy
Solids content: 52.0-58.0 %
Viscosity, 23℃: 400-500 mPa.s
Gel time (25 until 35 ℃): 33-43 min
Brand: AOC
Appearance: Clear
Solids content: 59.0-65.0 %
Viscosity, 23℃: 400-550 mPa.s
Gel time (25 until 35 ℃): 10-17 min
Brand: AOC
Appearance: Hazy – TM 2265
Solids content, IR drying: 48-53 %
Viscosity @23℃” 400-500 mPa.s
Gel time(25℃ to 35 °C) : 35-55 min
Brand: AOC
Appearance: Clear
Solids content, IR drying: 60-66 %
Viscosity @23℃: 300-500 mPa.s
Gel_Time (25 until 35 °C): 18-30 min