ZC-191 unsaturated polyester resin manufactured from raw materials like phthalic anhydride, maleic anhydride, and standard diols .The unsaturated polyester resin has been dissolved in the cross -linking monomer of the styrene, with medium viscosity and medium reaction activity.
| Supplier | |
|---|---|
| Resin Type | Unsaturated Polyester Resin |
| Pre-promotion Thixotropy | / |
| Molding Process | Hand Lay-up, Spraying |
ZC-191 resin features good strength and rigidity, fast post cure , excellent mechanical properties.
ZC-191 unsaturated polyester resin is widely used for ordinary glass reinforced products.
| Property | Value | Unit | TM |
| Appearance | Light yellow ransparent viscous liquid | – | – |
| Acid Value | 19-25 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.30-0.60 | Pa.s | GB/T 7193-2008 |
| Solid Content | 59-65 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gelation time,25℃ | 6-18 | min | GB/T 7193-2008 |
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Appearance:Light yellow transparent viscous liquid
Acid Value:20-26mgKOH/g
Viscosity，25℃:0.7-0.8Pa.s
Solid Content:62-68%
Thermal Stability,80℃:≥24
Gel time:6-18
Appearance:Light yellow transparent viscous liquid
Acid Value:19-25mgKOH/g
Viscosity，25℃:0.30-0.60Pa.s
Solid Content:59-66%
Thermal Stability,80℃:≥24h
Gel time:12-30min
Appearance:Light yellow transparent viscous liquid
Acid Value:14-20mgKOH/g
Viscosity，25℃:0.14-0.16Pa.s
Solid Content:52-58%
Gel time:25-38min
Appearance:Light yellow transparent viscous liquid
Acid Value:14-22 mg KOH/g
Viscosity, 25℃:1.6-2.3 Pa.s
Solid Content:70-76 %
Gel Time, 25℃:8.5-10.5 min
Thermal Stability, 80℃:≥24h
Appearance: light yellow transparent liquid
Density: 1.06±0.02kg/L
Viscosity: 430±150 cps (LVT#3-60rpm/25℃)
Solid content: 62±1.5%
Gelation time: 15-25 minutes