ZC-189TP resin is a pre-thixotropic unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard glycol as the main raw materials. It has low viscosity and medium reactivity.
| Supplier | |
|---|---|
| Resin Type | Unsaturated Polyester Resin |
| Pre-promotion Thixotropy | TP |
| Molding Process | Filament Winding, Hand Lay-up |
| Industry | Automotive & Transportation, Building & Construction, Marine Vessels, Petrochemical |
ZC-189TP resin meets the certification requirements of China Classification Society (CCS). It has good strength and rigidity, fast post-curing, is easy to wet the glass fiber, and does not flow easily during operation. It is suitable for hand lay-up process to produce ordinary FRP products such as small FRP boats in inland rivers and automobile parts.
| Property | Value | Unit | TM |
| Appearance | pink liquid | – | – |
| Acid Value | 17-24 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.3-0.4 | Pa.s | GB/T 7193-2008 |
| Solid Content | 58-64 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 25-43 | min | GB/T 7193-2008 |
Appearance:Yellowish transparent viscous liquid
Acid Value:14-20 mgKOH/g
Viscosity，25℃:0.35-0.45 Pa.s
Solid Content:61-67 %
Thermal Stability,80℃:≥24 h
Gel Time:4-6 min
Appearance:Light yellow transparent viscous liquid
Acid Value:20-26mgKOH/g
Viscosity，25℃:0.7-0.8Pa.s
Solid Content:62-68%
Thermal Stability,80℃:≥24
Gel time:6-18
Appearance:Light yellow transparent viscous liquid
Acid Value:14-20mgKOH/g
Viscosity，25℃:0.14-0.16Pa.s
Solid Content:52-58%
Gel time:25-38min
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %
Appearance: Clear liquid,no visible mechanical impurity
Epoxy Equivalent (g/eq): 176–184
Color (Gardner): Max 1.0
Flash Point (℃): Above 150
Viscosity (cps, at 25℃): 8000–11000
Hydrolyzable Chlorine Content (ppm): Below 1000
Specific Gravity (g/cm³, 25℃): 1.16
Appearance:Clear liquid,no visible mechanical impurity
Colour(Hazen):40 Max
Epoxy Equivalent(g/mol):210-230
Hydrolytic Chlorine (%):0.50 Max
Inorg.Cl （mg/kg）:50 Max
Volatile /150℃,40min(%):0.6 Max
Softening Point(℃):14-23