LOCTITE® FREKOTE® WOLO

LOCTITE® Frekote WOLO™ is a unique, low VOC polymer release agent that cures quickly and provides multiple release of all polyester resins. Applications and use of a release agent has never been easier, simply wipe on and leave on to produce a high gloss finish with no need to polish.

Additional information

Supplier

Additive Classification

Mold Release Agents

Industry

Automotive & Transportation, Building & Construction, Electrical & Electronics, Home Renovation, Marine Vessels

Typical Properties of Uncured Material

Specific Gravity @ 25 °C 0.71 to 0.73LMS
Flash Point See SDS

Directions for Use

  1. Apply LOCTITE® Frekote WOLO™ with a clean, lint free, cotton wiping cloth. Wet the cloth with LOCTITE® Frekote WOLO™ until it is damp but not dripping.
  2. Wipe a smooth, wet film over the entire mold surface. For larger molds, apply LOCTITE® Frekote WOLO™ to the surface one section at a time starting at one end and working towards the other. Continue to work the material into the mold by lightly wiping the wet film (10-30 seconds) until a thin and uniform coating is obtained, and then allow the product to evaporate.
  3. Allow a minimum of 5 minutes before applying next coat. Apply a minimum of four coats in this manner. Dampen cloth lightly as needed.
  4. Allow the final coat to cure for 15 minutes at 20°C.
  5. NOTE: If the cloth dries out during your coating process, use a fresh clean cloth to apply the next coat. This prevents resin accumulation on the cloth from being deposited on the mold surface. If streaking occurs, replace the cloth with a clean dry one and/or make sure that the cloth is just damp and not soaking wet. Avoid over-application, as this will cause streaking on the tooling surface. Streaks or wipe lines can be removed easily by wiping the mold surface lightly with a dry cloth. Product is moisture sensitive, keep container tightly closed when not in use.
  6. NOTE: For maximum number of releases, apply a touch up coat after the first 2-3 parts are released as a break in period after the initial application. On deep or high wear areas, apply an extra 1-2 coats of LOCTITE® Frekote WOLO™. This will help increase the slip even further in these high drag areas.

ZC-5885

Brand:Polylite
Appearance:Transparent, water-white liquid with a bluish tint
Viscosity:0.75-1.25 25℃, Pa.S
Gel Time:5.6-10.4 25℃, min
Acid Value:18-26 mg KOH/g
Solid Content:64-70 %

ZC-44

Brand:Polylite
Appearance:Clear liquid,no visible mechanical impurity
Colour(Hazen):40 Max
Epoxy Equivalent(g/mol):210-230
Hydrolytic Chlorine (%):0.50 Max
Inorg.Cl (mg/kg):50 Max
Volatile /150℃,40min(%):0.6 Max
Softening Point(℃):14-23

#333MR: Blue Wax

True high-gloss paste wax.
Withstands high-temperature exothermic reactions of resins and does multiple releases easily.
Contains carnauba wax, synthetic waxes and high-temperature resistant resins for effective multiple releases of plastic parts through numerous cycles.

Trigonox K-90

Brand:Trigonox®
Chemical family:Organic peroxide
CAS number:80-15-9
Physical form:Liquid
Molecular Weight:152.2
Chemical name:Cumyl hydroperoxide

Butanox M-60

Brand:Butanox®
Chemical family:Organic peroxide
CAS number:1338-23-4
Physical form:Liquid
Chemical name:Methyl ethyl ketone peroxide

ZC-638

Brand:Polylite
Appearance: Semi-solid
Epoxy equivalent (g/eq): 170-190
*Hue(G): 3.0Max.
Flash point (℃): 250↑
Solution viscosity (25℃): H~K
Density (g/cm³ 20℃): 1.18